Electronics Forum | Thu Apr 12 20:27:10 EDT 2001 | davef
Tantalum caps degrade over time. You should not be seeing "chipped-off & cracks" regardless of the age. This should not be a shelf-life issue, unless you are storing them in an aquarium. Tell us the story. Solderability is a shelf-life issue and
Electronics Forum | Tue Apr 10 23:33:50 EDT 2001 | zam_bri
Hi.. What is the typical shelf life for chips capacitor 0603/0402 and what is the consequences of using the capacitor which more than 1 year old esplly on double reflow process. Pls help and thank you in advance. cheers
Electronics Forum | Thu Dec 16 23:17:02 EST 2010 | Jacki
Hi Kim Dun take any risk in delamination bcoz u will be the person to answer for being it. So, we do bake all Pcbs, which have 3months of shelf life, b4 startin any process although they are still inside the factory packs.
Electronics Forum | Fri Sep 09 05:29:25 EDT 2016 | jasltd
simpel answer is yes it will need to be baked, the typical shelf life for a sealed component assuming it has been sealed would be a max of 2 years but some are shorter. The bugger problem with the device may well be solderability of the device!
Electronics Forum | Thu Nov 03 08:34:25 EST 2005 | Slaine
Hi We currently use a small amount of Alloy : 43Sn 43Pb 14Bi Flux: RMA-51AC, Metal : 88.5%. We use it for reworking a product and only consume about 100g per year, we are in the middle or ordering in some more paste but the MOQ is 500g. Is it possibl
Electronics Forum | Wed Apr 11 10:28:02 EDT 2001 | davef
What's the issue? Solderability or performance of the component
Electronics Forum | Thu Dec 16 09:15:07 EST 2010 | davef
Please post pictures of microsections
Electronics Forum | Mon Jan 05 00:30:07 EST 2004 | Arthur Yang
Hi you there, Do you have any experience upon the shelf life of PCBA which passed 100 cycles of liquid to liquid thermal stress test, 125 to -35 centigrade for 15 minutes and 5 seconds of transfer time from 125 to -35 centigarde. Will apprecia
Electronics Forum | Fri Dec 17 03:26:04 EST 2010 | kemasta
Thanks. If based on your statement, I can understand why it still can absorb moisture. But the PCB supplier was suggested us to keep at 40%~70% RH, if any issue occur with the storage condition of less than 5% RH, I think it is difficult for us to ge