Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? What are the limitations? Thanks, Steve
Electronics Forum | Fri Aug 28 23:32:39 EDT 1998 | Pete Sorenson
| Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? | What are the limitations? | Thanks, | Steve I have used silver epoxy extensively for conductive bonding applic
Electronics Forum | Thu Feb 12 21:30:45 EST 2004 | davef
Comments are: * We're amazed that you can thermocompression bond to epoxy. * Silver may be oxidizing during expoxy cure. * Klein Wassink talks about aging in THE BOOK [Soldering in Electronics: A Comprehensive Treatise on Soldering Technology for Sur
Electronics Forum | Thu Aug 27 17:40:11 EDT 1998 | Earl Moon
| Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? | What are the limitations? | Thanks, | Steve Steve, Hello again. Hope you guys (Intel) aren't going to do that
Electronics Forum | Thu May 22 14:16:40 EDT 2003 | MikeF
We need more information to give you a good answer. Is this a leaded part (axial or radial) or smt? How big is the part, how much weight per lead? What is the end use environment, will it see any vibration? or temperature extremes? Some general com