Electronics Forum | Tue Aug 30 09:24:08 EDT 2005 | Slaine
we manufacture a range of ceramic parts that have silver termination,there is already a small leaching problem (absorption of the termination by the solder in liquid form)with Sn62 that we live with, having to implement unleaded solder they are norma
Electronics Forum | Tue Aug 30 12:49:59 EDT 2005 | Ted
Slaine, We use a Pd/Ag thickfilm paste. Because of the leaching we had to start using solder pastes that have silver in it. For RoHS, we are using a solder paste with an alloy of Sn95/Ag05. We also have to double print the thickfilm pastes. I h
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so