Electronics Forum | Tue Jun 27 10:30:54 EDT 2006 | russ
Aj, Did you switch from SN100C to the SACX? Russ
Electronics Forum | Tue Jun 27 09:25:55 EDT 2006 | aj
How does SN100C perform using Selective Pallets? We switched over to SACX about 5 weeks ago and the results are brilliant. We are getting better results than before believe it or not. Also dross foramtion is a lot less. aj...
Electronics Forum | Tue Jun 27 01:41:42 EDT 2006 | grantp
Hi, How come so many good threads get off track because of this Guru fool. To get back on track, we have been running SN100C in our pot for a few weeks now, and it's incredible, and working really well. Glad I listened to the advise of people on th
Electronics Forum | Mon Jun 12 07:27:19 EDT 2006 | amol_kane
thanks Jay,
Electronics Forum | Mon Jun 26 10:45:14 EDT 2006 | russ
I contacted you about this stuff, where is the info?
Electronics Forum | Tue Jun 27 10:41:20 EDT 2006 | aj
No. We went straight from Lead Alloy to SACX. aj...
Electronics Forum | Fri Jun 30 20:39:52 EDT 2006 | johnwnz
Grant, Haven't doen any work with the SN100C paste, the problem I guess is yoru subject to the suppliers flux base so if that is poor then the alloy may not perform as well as it could. We've found Avantec to be pretty good at SMT but have got SN100C
Electronics Forum | Fri Jun 09 07:26:24 EDT 2006 | amol_kane
hi, gald to hear that yr process is working well.....we are in the process of buying a wave with SN100C solder.....any pitfalls/precautions that you took during the transition? did you do any DOE for setting up the profile values?? are you seeing a
Electronics Forum | Tue Jun 27 08:38:03 EDT 2006 | cuculi54986@yahoo.com
I tried some SN100C from AIM... On only one array. It flowed well on the chips but did not like the finish on the SOT23's on the board. I did not have enough arrays to mess around, so we switched it over to SAC305 and had no issues. I'm guessing w
Electronics Forum | Thu Jun 08 19:51:22 EDT 2006 | grantp
Hi, That's good news, and we did outs with SN100C as well on Wed, however we are still working hard on getting a good profile. We have some large BNC connectors, and they are hard to profile. We also have wave palettes, and these might be too thick