Electronics Forum | Sun Apr 24 09:12:00 EDT 2005 | davef
We're not sure what your customer is talking about either. Gold and tin form an intermetallic compound [IMC] that can cause poor solder connections. To minimize the potential of a problem, keep gold to less than 3 percent of the metal. [Search the
Electronics Forum | Tue Apr 26 07:56:12 EDT 2016 | joelperez
Hello SMTnet team, I have read before that silver content on solder joints is ok at around 2% total silver content. Does anyone has experience using SN62/PB36/AG2 BGAs on hard gold (10 micro inches) PCB surface finish? Any drawbacks? Thanks Joel
Electronics Forum | Thu Apr 15 09:45:34 EDT 1999 | Terry Keen
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Apr 13 08:08:33 EDT 1999 | Rob Palson
We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to bu
Electronics Forum | Mon Apr 19 02:38:41 EDT 1999 | Brian Sloth Bentzen
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Thu Apr 15 08:21:47 EDT 1999 | Terry Keen
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Fri Apr 16 11:07:53 EDT 1999 | Vic Lau
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Apr 13 09:11:54 EDT 1999 | Dave F
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Tue Apr 13 17:44:29 EDT 1999 | Christopher Lampron
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Mon Apr 19 02:45:31 EDT 1999 | Brian Sloth Bentzen
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t