Electronics Forum | Fri Jul 06 12:11:34 EDT 2007 | james
We are starting to see issues with using Kester WS R562 with lead free components. The joints look grainy on almost all of the 0402'2 and other small components. Some of the solder does not solder to the terminations. These are hybrid boards which
Electronics Forum | Fri Jul 06 13:44:15 EDT 2007 | shrek
Krikies! seems like a head-scratcher if I may say so me-self. I would say the other ogre is right, that surface finish will play a big factor in your solder joint's grain structure or how shiney 'tis. Non-HASL bearing finishes will typicaly exhibit
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN
I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f
Electronics Forum | Tue Aug 31 11:57:03 EDT 2004 | Kris
Hi Any body have any issues soldering tin lead solder paste with lead free terminations ? Components are leaded devices and chip components have read the theoritical discussions on the forum, need to know if any body has seen any real issues tod
Electronics Forum | Mon Apr 09 19:50:33 EDT 2012 | action_101
Hello, We're building some boards with 01005's and the only issue we are running into is the solder is not reflowing. It's the damnest thing, we are having no issues with the printing process or placing the components, the two areas we thought we wo
Electronics Forum | Wed May 24 16:19:58 EDT 2006 | inds
John, there have been quite a few discussion on Mixed Assemblies in this forum.. do a search.. you will get whole lot of information.. in addition - IF you are using Lead-free reflow profile...make sure the rated temp for Sn-Pb components is not vi
Electronics Forum | Mon Jul 28 14:30:22 EDT 2008 | grics
Take a look at this. Remember, these are only guidlines and can not replace any paste specs. As Real Chunks said, a profiler will be of HUGE help. We use this to determine what our top side temps are and to see if we have any problems with heat sen
Electronics Forum | Wed May 24 16:40:40 EDT 2006 | samir
Yikes! Sounds like a hairy situation there. I've successfully collapsed a Pb-Free BGA (using a Sn/Pb solder paste), with a peak temperature of 220 Deg. C and Time Above SAC's Eutetic point (217) of 17 seconds. Beware of overcooking your smaller ma
Electronics Forum | Wed Sep 18 12:31:16 EDT 2002 | dragonslayr
My suggestion is to conduct a Design For Manufacturing (DFM)study on the assembly in question. Pay particular attention to the pad sizes, component lead dimensions and satisfy yourself that those two factors are correct. Given that pads match compone