Electronics Forum | Mon Sep 12 10:41:50 EDT 2011 | processmxli
Hi All We have run SMT process with SnPb but we’re installing some lead free components like capacitors and resistor lead free. After the reflow oven all components have good appearance with solder join sheen. But the lead free components the solde
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Mon Jul 16 11:04:21 EDT 2007 | davef
You want published articles? Look here: http://www.google.com/search?sourceid=navclient&ie=UTF-8&rls=GGLC,GGLC:1969-53,GGLC:en&q=leadfree+in+snpb
Electronics Forum | Mon Jul 16 10:26:54 EDT 2007 | davef
Ed: We agree with you that leadfree parts can be used with leaded paste. We disagree that lead part can be used with leadfree paste. Here is link to a previous discussion here on SMTnet on the topic: http://www.smtnet.com/forums/Index.cfm?CFApp=1&M
Electronics Forum | Fri Jul 06 12:11:34 EDT 2007 | james
We are starting to see issues with using Kester WS R562 with lead free components. The joints look grainy on almost all of the 0402'2 and other small components. Some of the solder does not solder to the terminations. These are hybrid boards which
Electronics Forum | Mon Jul 16 10:17:22 EDT 2007 | realchunks
Yes you can use no-lead parts in a leaded process. Your solder joints will be weaker than they once were unless you change your solder paste. You can try to improve this by running a hotter reflow temp, but be careful since your flux was not design
Electronics Forum | Thu Jul 19 11:59:21 EDT 2007 | hussman
Phil is wrong. In the real world, we know that part mfgers have not changed every one of their parts to make them "high temp". They just changed the plating. Anyone who thinks otherwise, has never run a profile or touched a warm board coming out o
Electronics Forum | Thu Jul 19 04:38:33 EDT 2007 | chrispy1963
I took a Lead Free troubleshooting Class at SMTA in Chicago last September taught by Phil Zarrow. He told us during that seminar that its not a good practice to cross contaminate Leaded and Lead Free components but IF it is necesary than using lead
Electronics Forum | Fri Jul 20 08:09:09 EDT 2007 | chrispy1963
In passives I dont know if anything changed at all other than the terminal plating. As for Active components there has been much engineering done to allow for the extra heat needed to liquify say SAC305 or other lead free pastes without damage to th
Electronics Forum | Mon Jul 16 10:51:09 EDT 2007 | patrickbruneel
D. Hillman, et al., �The Impact of Reflowing a Pb free Solder Alloy Using a Tin/Lead Solder Alloy Reflow Profile on Solder Joint Integrity,� International Conference on Lead-free Soldering, CMAP, Toronto, Ontario, Canada, May 24-26, 2005, http://www.