Electronics Forum | Wed Nov 29 00:43:45 EST 2006 | callckq
Dear all, Recently, we run 2 models with heat sink attachment on top of this BGA(on top of this BGA, there is flip chip attached at the center of the BGA). Hence, the center of the BGA is higher than corner/side. We used conventional way to attach
Electronics Forum | Wed Apr 21 17:11:05 EDT 1999 | Earl Moon
| Does anyone have any experience with soldering 50mil pitch BGA's that have a via in the pad, the size is .012 The via will be masked off on the bottom side of the board. Need to know what precautions or problems if any I might encounter. The proces
Electronics Forum | Wed Apr 21 19:09:10 EDT 1999 | Earl Moon
| | Does anyone have any experience with soldering 50mil pitch BGA's that have a via in the pad, the size is .012 The via will be masked off on the bottom side of the board. Need to know what precautions or problems if any I might encounter. The proc
Electronics Forum | Fri Jul 23 14:41:41 EDT 2004 | Steve Stach
Dear JSK, It sounds like the root causes of your problem are two fold. First, excessive heat will polymerize the abietic acid found in rosin forming neo-abietic diamers and polymers which are much less soluble than the parent monomer. There are
Electronics Forum | Thu Mar 25 09:14:09 EDT 2010 | krish_bala
Hello, I have been having some troubling issues when it has come to BGA Placement and I was hoping if there have been others who have been able to resolve similar issues. We are curently doing reworks on a variety of BGA, but seem to be having issu
Electronics Forum | Wed Sep 22 22:18:37 EDT 1999 | Dave F
| I am attemping to gather as much information on the issues with and progress in solutions for manufacturing Pb free products in response to European initiatives (WEEE). I am intereested in component issues with As Made lead terminations (no Sn/Pb)
Electronics Forum | Wed Oct 25 10:11:09 EDT 2000 | Wolfgang Busko
Paddesign, aperture size and stencil thickness determine the amount of solder for your joint. Once you have found suitable parameters you need to control the volume of your paste deposit which is influenced by printer settings, paste condition, stenc
Electronics Forum | Wed Sep 20 19:34:13 EDT 2000 | Dave F
Congrats. You now control the source of almost 70% of the defects of your SMT operation. There is a neat series of presentations on printing, each year at SMI. One of the best of the SMI series was in 1997, because presenters used a common board
Electronics Forum | Thu Apr 05 12:25:17 EDT 2001 | Adam
The Solderballs are on the botton side of the board.The solderballs are concentrated around through hole edge connectors, which have a Tin/lead finish and have lead pitch of 2.5mm, on top of this, random solderballs are occuring around test points. T
Electronics Forum | Fri Nov 26 09:13:10 EST 1999 | Wolfgang Busko
Jeff, Ted, Stefano What Stefano is saying sounds reasonable. With entry-level systems its always a struggle to get sufficient results. The operators golden hand is needed. Better controlled advanced dispensing systems should do the work, unluckily I