Electronics Forum | Thu Jun 03 14:40:22 EDT 1999 | JohnW
| | | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. W
Electronics Forum | Thu Jun 03 14:41:06 EDT 1999 | JohnW
| | | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. W
Electronics Forum | Sat Jul 16 16:21:56 EDT 2005 | Mark
Should solder paste be placed back in the refrigirator after use? If so, is there a limit on how many times we may take it out and re-refrigirate it? After receiving solder paste, it is put away in the fridge. Then, removed a few hours before use
Electronics Forum | Thu Sep 16 09:29:21 EDT 2010 | san_1023
Weller and Hakko have some good soldering > stations, hot air SMD rework system and BGA > rework systems: _a class=roll > href="http://www.wellersoldering.blogspot.com/" > target="_blank"_http://www.wellersoldering.blogspo > t.com/ _/a_ I am t
Electronics Forum | Thu Jan 05 15:42:26 EST 2006 | samir
Grant, The strength of the joint in a CCGA is the column for one...it's more ductile, made out of 90% Pb, and it's meant to compensate for the massive CTE mismatches between the ceramic and the board (ie the columns flex to relieve stress from the e
Electronics Forum | Sat Oct 02 20:19:19 EDT 1999 | John Dwinell
| | I am currently in the middle of a company wide war and I'm looking for data (AMMO). Here are the problems: | | | | 1) I am looking for anyone who has done or seen any reports on Thermal Shock to smt parts and/or via holes caused by Soldering Ir
Electronics Forum | Mon Jul 24 22:50:43 EDT 2017 | dawson
In fact, we can solve this problem easily. AOI only check whether the IC is soldered well. But we can ask our technician to make a test first to control the reflowing temperature and time. 1. using tool to test the temperature between the bottom IC
Electronics Forum | Wed May 11 11:36:43 EDT 2005 | rlackey
Hi Peter, There is no Silver in it, which even in small quantities (0.3%-4%) improves solderability. I would try and see a demo on a similar machine to yours with a similar product as everyone can get their solder to look great in lab/showroom site
Electronics Forum | Thu Oct 18 08:27:46 EDT 2018 | spoiltforchoice
They visited our factory once bringing the desktop variant with them quite a while ago (~8 years perhaps when they were still called something else). At the time it was an FAI machine first and foremost with some "AOI like" features that perhaps o
Electronics Forum | Thu Jul 15 21:26:01 EDT 1999 | Scott McKee
| I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | What is it you're trying to do? Dealing with chem