Electronics Forum | Thu Nov 19 14:38:49 EST 2009 | doremi
Oh, my dear, printer is just a part of the full picture. Without good and stable pick and place what if the printer is excellent???It is all important - printer, solder paste,stencil,P&P,oven,AOI and of course good process engineers or whatsoever are
Electronics Forum | Wed Aug 30 16:00:42 EDT 2000 | Dave F
Russells: You can mix the two solders you mentioned, assuming by "96s" you meant "96Sn / 4Pb". If you heat the two tin / lead alloys to a liquid state, you�ll form a tin / lead solution with properties different from either of the two solders. The
Electronics Forum | Tue Jul 29 12:51:40 EDT 2008 | grics
I am having some problems with some of my pcbs at ive solder. We are using an ersa versaflow. It has an automated spot/spray fluxer (Interflux Pacific 2009M) , 1 preheat stage, a leaded pot/nozzel, and finally a lead-free pot/nozzel. Nozzels move, b
Electronics Forum | Sat Jul 29 00:44:30 EDT 2000 | Jason
Thanks for all the ideas. I tried solder "thieves" by placing some desoldering wick behind the briging pins and it worked! I have yet to try Chrys' idea but I will first thing Monday. This is a new board that has had this problem from day one. I
Electronics Forum | Fri Mar 02 08:52:20 EST 2001 | markkrmp
Are your voids looking like blow holes also? Is this only occurring on the solder joints of the Thru Hole components and Via's? Or does this happen on SMD pads? My experience is that we have seen this but only with some of our older PCB's which are
Electronics Forum | Thu Mar 22 16:35:06 EST 2001 | Steve
Deja vu! When I read your response I turned around to see if you standing behind me listening to our problem. We currently make about 50 different boards all using no-clean that have no problems, yet this newest boards has a couple of issues that eng
Electronics Forum | Wed Dec 18 10:10:07 EST 2002 | davef
No, sorry not on "Dave's Bookshelf". My basis is a study done at IBM. I reference it here: http://www.smtnet.com//forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=4941&#Message19050 Responding differently, you're correct. If you have a
Electronics Forum | Thu Feb 13 10:15:09 EST 2003 | dwanzek
Bridges are front to back. To me this seems to indicate thieves would pull the solder away from the pins. I feel I am correct in that theory. Yes, it would be a good idea for us to bring in a consultant but I have the opportunity right now to make b
Electronics Forum | Wed Jul 02 12:42:58 EDT 2003 | slthomas
Not sure how else to describe this. We've received some boards (1/2" x 3.5" x .0325" board built on panels of 24) with numerous resistors showing separation of the solder from the metallization at the top of the joint. There are 26 0805's on the bo
Electronics Forum | Tue Dec 21 11:46:29 EST 2004 | KEN
Are you adding liquid flux? Or paste "Gel" flux? If liquid flux: This, in my mind, is an unacceptable technique. Why? 1. Can not control metals content. 2. Probably not adding the same chemestry flux...as paste flux has many different addi