Electronics Forum | Mon May 22 12:04:03 EDT 2000 | Michael Parker
80%. There are too many factors at hand to point the finger yet. We need to build a truth table and dot the i's and cross the t's before stepping up to Goliath (Samsung). Is you placement guranteed good? What x-ray have you used? Are your fab.'s know
Electronics Forum | Fri Jun 08 14:19:35 EDT 2001 | Spanky
Jake, The No-cleans on the market, to me, still aren't as good as OA and water wash. But they have gotten better. The type of No-Clean flux and paste to use really depends on each individual assembly, the machines used, settings, and the environme
Electronics Forum | Fri Jul 24 12:02:06 EDT 1998 | Steve Gregory
Stoney, One thing you might do before you start dispensing epoxy, (...I know this might be a bit of a pain) is to run your boards on the mesh belt instead of the edge-rail conveyer. I used to have to do that with some very,very dense double sided mem
Electronics Forum | Sun Dec 22 11:02:44 EST 2002 | valuems
I am breaking a cardinal rule with this reply, but here goes. I believe almost every one is missing this one. Roger has hit the nail on the head. The gentleman is useing a clam shell printer and when the stencil lifts (too fast) and at the angle o
Electronics Forum | Tue Feb 17 17:55:38 EST 2004 | bman
I might be saying something that will get me laughed off of SMTnet forever, but when faced with a similar problem here's what I did. Since I was removing parts I didn't see why I would be concerned about all the things that go on in a good temperatu
Electronics Forum | Mon Apr 02 09:24:16 EDT 2007 | ed_faranda
I do this ALL the time, and it is pretty much transparent to the process. We have done shake, burn in, and functional tests with our products and we didn't have any issues what so ever. We have had a RoHS complient process for well over 18 months n
Electronics Forum | Tue Oct 28 20:26:53 EDT 2008 | fishingfool
Dominik, Pixel size should not be the main criteria for selecting an AOI. I have a customer that has 2 MVP and they say the solder test are good but part reconigtion is not so good. You also say you need some flexibility on software. I also have
Electronics Forum | Wed Feb 08 09:21:03 EST 2012 | ngineer
What Should I use to clean a sticking conveyor > belts in my pick an place machine (Quad IVc)? > The belts seem to have what I would guess to be > solder paste that is dried, but also they seem to > be a bit gunked up as if they had gotten some o
Electronics Forum | Wed Oct 13 04:30:01 EDT 1999 | Brian
Hi! I recently remarked on a thread that so-called VOC-free fluxes weren't. As a result, I got three private e-mails asking what I meant. As this seems to be unclear, I'm starting a new thread with my explanation, rather than sending out the answers
Electronics Forum | Thu Sep 09 22:18:13 EDT 1999 | Dave F
2 will have enormous impact on every other process. | | | thank in advance. | | | scott. | I appreciate your sincere answer. | would tell me the hint about printer if i's possible | To tune our smt process we have to know what is the major X