Electronics Forum | Wed Feb 26 13:26:24 EST 2020 | rgduval
I'd agree with getting a stencil fully cut, and taping the pads you don't want paste on. But, I'd also check with the people that will be doing the hand soldering to see what they prefer. Some people prefer soldering on bare pads, some prefer solde
Electronics Forum | Tue Oct 06 15:01:33 EDT 2020 | charliedci
We've used glass (pyrex, corningware) bread pans in the past, not filling them much over 1" deep. It takes a while but leaves solder ingots sized well to drop back in. Have not tried lead free yet, the higher temp could be an issue using same ty
Electronics Forum | Thu Jun 24 04:38:31 EDT 1999 | Vinesh Gandhi
Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody help
Electronics Forum | Fri Feb 05 09:39:58 EST 1999 | Dave F
| Can anyone help me with the pros and cons of trying to wave | solder tantalum and large (1812) ceramic capacitors. I do | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what proble
Electronics Forum | Fri Sep 21 01:31:13 EDT 2001 | Stoney Tsai
Guys, If there are any specifications or ciriterions for solder paste deposition thickness and volume evaluation. For example, QFP (0.5 mm pitch), 6~8 mils, 3000 mil^3 PLCC: 8~10 mils, ... . . Thanks in advance. Best Regards,
Electronics Forum | Sun Sep 12 21:08:07 EDT 2004 | mksslcheng
Could someone recommend me the manufacuter who is produce Kapton tape or Alum. tape or Epoxy ,I want to profile wave soldering .You would be appreciated if you can provide its website .
Electronics Forum | Fri Oct 05 11:14:14 EDT 2007 | Frank
Yeah, but when the operator drops regular solder bars into your lead-free pot, does that mean I should paint my bars, too?
Electronics Forum | Thu May 01 21:17:38 EDT 2008 | davef
The concern about lead contamination of lead-free solder has to with zone refining. For more, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=30315
Electronics Forum | Wed Aug 15 04:08:04 EDT 2018 | colinbenton
Hi Stephen, it seems they call it differently . What they need is an insruction data they can import to the machine, how the IC is soldered, the relative orientation for some parts,ect.
Electronics Forum | Mon Apr 29 22:25:30 EDT 2019 | pcbindex1
Besides, regulated power supply should be installed separately on the printing boards. When power and circuits share the same printing boards, it should be avoided that regulated power supply and circuit components are mixed or power and circuits sha