Electronics Forum | Tue Oct 12 04:18:12 EDT 1999 | Scott Davies
| | We have three buckets filled with leftover solder paste from our screen printing process. Kester has informed me that they no longer take paste, but only dross and pot dumpings. Does anyone know if there's someplace I can recycle this, or am I
Electronics Forum | Tue May 26 13:01:40 EDT 1998 | Earl Moon
| Regardless of what various inspection standards state, has anyone got any information on how the strength of a soldered joint changes with the amount of solder in contact with the legs. ie if there is 0.152um depth of contact how does the joint st
Electronics Forum | Wed Dec 15 21:29:34 EST 2004 | davef
We�d say that it�s incorrect that ENIG solderability protection cannot be steam aged. It�s true the immersion tin and silver cannot be steam aged. We believe that most of the issues surrounding the poor performance of ENIG after steam aging is attr
Electronics Forum | Fri Dec 27 02:11:31 EST 2019 | anteiv
Hello, We are having problems with SMD wave soldering (ERSA) used flux is BALVER ZINN 390-RX-HT https://www.balverzinn.com/tl_files/balverzinn/downloads/intern/TDB/PDS_390-RX-HT_EN.pdf https://www.balverzinn.com/tl_files/balverzinn/downloads/datenb
Electronics Forum | Fri Apr 13 22:56:02 EDT 2001 | gdstanton
I've been chipping away on a solder bridging and poor fillet wetting problem for a few weeks now (new to the company) and I found two issues. First, after a review of stencil inventory, I found apertures to be oversized when compared to suggested di
Electronics Forum | Sat Jul 25 04:57:17 EDT 1998 | Stoney Tsai
| I have been building one sophisticated SMT soldering expert system (KBS), through my 8-YEARs SMT experience. As I know, in the marketplace only published some SMT raw material selection Expert System. | The system needs more technical information a
Electronics Forum | Thu Feb 15 23:52:31 EST 2001 | Dreamsniper
Hey guys, I ran a couple of profile in our wave solder machine using wave optimizer and this is what i got: Parallelism = 0.0 Immersion Depth = 2.1mm to 2.4mm with varying immersion time from 1.1 sec to 3.1 secs. Contact Length = between 5.0 to 6.0
Electronics Forum | Tue Sep 21 16:09:08 EDT 2004 | davef
Q1: What is "enough surface free energy"? A1: Look here for background: http://www.azom.com/details.asp?ArticleID=1575 Q2: How do I determine surface free energy? A2: We look at it a relative term. For instance, a semi matte finish on solder mask
Electronics Forum | Sat Dec 17 08:07:06 EST 2005 | grantp
Hi, What worries me is that a lot of people speak about what they have heard, but there is no firm facts on exactly what the situation is. I did a seminar on lead free a while ago, and was told that going lead free on the components while running l
Electronics Forum | Thu Oct 14 10:49:13 EDT 1999 | Dan Woodward
Andrew, As I read about issues with reworking connectors, whether they are surface mount or PTH soldered, I wonder if compliant pin pressfit connectors are being considered. They are easily assembled after all SMT without any thermal input, and on e