Electronics Forum | Tue Jun 03 18:34:22 EDT 2003 | Kris
Hi, There have been other studies where it was found that lead-free soloder joints are more reliable than tin-lead solder joints irrespective of test conditions. In fact the automotive industry has been using Sn/Ag for underhood applications for a
Electronics Forum | Thu Jun 05 06:03:49 EDT 2003 | iman
Japan and Europe are the main champions for the leadfee solder initiative. USA join in due to global political efforts as one of the cub scout leaderships. Military and Automobile industrial-electronics is exempt from the leadfree directive. Reason
Electronics Forum | Wed Jul 27 16:46:48 EDT 2005 | russ
I don't think that you would need to test these. Have you ever seen any evidence of solder sticking to them? We use the same material and never notice anything besides flux staying on the bottom. Would the lead absorption if any even be of a concer
Electronics Forum | Sat May 15 11:27:26 EDT 2010 | davef
We'd expect both OSP poor wetting and improper reflow recipe to show-up in more places than just this one component. But if those are the only choices, we'll go for 'wrong solder paste.' Ooops, that's not one of the choices. Ok, OK, we'll take poo
Electronics Forum | Tue Jun 03 12:24:50 EDT 2003 | blnorman
I have received information from the European Commissioners Environmental group that automotive electronics are not covered by WEEE (waste electrical and electronic equipment 2002/96/EC) or RoHS (reduction of hazardous substances 2002/95/EC) because
Electronics Forum | Fri Apr 06 08:27:09 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Proctective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyimide with electroptical connecti
Electronics Forum | Fri Apr 06 08:28:34 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Protective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyamide with electroptical connectio
Electronics Forum | Mon Oct 29 18:21:43 EST 2001 | slthomas
We recently have received a lot of warped (bowed and/or twisted behond IPC 600 specs.) bare boards (some our fabricator's fault, some ours by design) and I can't help but figure that long term reliability will suffer when building product with them.
Electronics Forum | Fri Apr 06 08:36:13 EDT 2001 | Cal
Sorry about the double post.........my Vanna White spell check crapped out on the first reply.
Electronics Forum | Fri Aug 01 00:30:04 EDT 2003 | caldon
Also Try: http://www.airliquide.com/en/business/industry/electronics/expertise/tech_papers.asp you can also search the airliquide site for "PPM" once in the electronics section Cal