Electronics Forum | Sun Apr 05 09:25:12 EDT 1998 | Earl Moon
| Dear Peter, | out of the manufacturers sight, Steve is 100% right. | The manufacturer gives a guarantee for at least | 6 Month because we know from our own test, that | the homogenity is one of the most important parameters | for a good printabilit
Electronics Forum | Sat Mar 09 07:09:44 EST 2002 | davef
Interesting findings. I agree that probably no one does �100% volume measurement and subgrouped Xbar and S charts�. Who would want to spend the money? Isn�t the issue making things, rather than measuring things? The microscope is used to make m
Electronics Forum | Mon Jun 17 21:18:24 EDT 2002 | davef
I don't understand "well we can't paste the flip chip on its substrate because we are using flux". There is flux in paste. What's the difference? If you use solder paste, there will be more room for underfill, as compared to flux only. Some peopl
Electronics Forum | Thu Sep 25 12:59:14 EDT 2003 | successmani
hi, I am a research student in Electronics manufacturing at RIT. We are planning to assemble boards using lead free solder paste. I was wondering would there be any changes in printing in using lead-free paste"Sn-3.9Ag-0.5Cu". Thedensity of Sn-37Pb
Electronics Forum | Mon Jan 29 09:50:37 EST 2007 | rgduval
I'm about to begin a job for a customer placing a couple of lead free BGA's/FPGA's on an assembly that doesn't need to be RoHS compatible. So...my question is...should I process this assembly with lead-free solder paste, to accomodate the lead-free
Electronics Forum | Sat Apr 07 01:15:45 EDT 2007 | Haris
Hi I dont think there is a stencil problem or a printing one but i think you should check you paste specification regarding 20 mil pitch i.e. its ball size in microns so that you know Is that paste can be use for this type of components or not. Secon
Electronics Forum | Fri Apr 13 12:24:07 EDT 2007 | teamcanada
We assemble for a customer that is having an inconsistent low level analog interference we believe with the no clean flux residue from Alphas OM5100 solder paste. We are considering testing Amtechs 4300 water washable no clean paste. We will test bot
Electronics Forum | Fri May 11 10:59:39 EDT 2012 | 14367
Thank very much for the feedback. I was asked why mixing the paste was not a good idea. Could you provide the answer please? It's always better to hear from an outside expert:) The SOT23 - some of them have actually flipped upside down ; plus we hav
Electronics Forum | Fri May 31 12:50:42 EDT 2013 | spoiltforchoice
Is this a "thermal balance" issue? In the 2nd image you have a group of pads blobbed together as one giant pad. IMHO this is a bad idea, QFN's rely heavily on the magic of your paste and good PCB design to get good alignment. When your solder paste i
Electronics Forum | Tue Mar 27 01:46:59 EDT 2018 | buckcho
Hello, can you tell me your SPI machine brand? Some brands have Bare board teaching for getting the best data when measuring paste. Even then it is normal to have more paste than 100%. So you can check your average and see if you are getting this on