Electronics Forum | Thu Oct 24 15:02:16 EDT 2002 | seand
Hello Yannick, Have you brought this concern up with your supplier? I would recommend speaking with your flux and paste provider to gain additional insight and recommendations for resolving the concern. Good luck, Sean D.
Electronics Forum | Tue Sep 09 15:10:01 EDT 2003 | swagner
Has anyone had negative experiences with hasl thicknesses below .00005'' of an inch on copper? If so could you please respond with what the problems were. Thanks in advance!!!
Electronics Forum | Fri Sep 26 12:57:09 EDT 2003 | Angie
We have had some components that popped off in our IR oven. It was attributed to the solder paste. The humidity was above 60% the temp was about 70 degrees.
Electronics Forum | Thu Jul 14 10:00:21 EDT 2005 | chunks
Any one using SPC to monitor their wave solder process? My point is collecting defects and using a scatter plot is useful but only after a problem occurs. SPC's true function is to warn of impending problems that are about to occur. Can SPC really
Electronics Forum | Thu Jul 14 10:37:15 EDT 2005 | pjc
Here are links to the web sites for three instruments specifcally designed to monitor wave solder process. Some have SPC logging capabilities: http://www.ecd.com/emfg/instruments/waverider/ http://www.swpc.co.il/wso.htm http://www.solderstar.com/w
Electronics Forum | Fri Jul 15 09:43:37 EDT 2005 | dougs
HHmmmm!! looks like i'm getting it way wrong by wanting to chart the quality of product coming from my wave solder machine. could some of you let me know whats the best way to monitor quality on this process.
Electronics Forum | Wed Aug 31 12:33:25 EDT 2005 | Jaya
I have expirence running,double sided Imm gold boards recently which ed up a lot of solderability issue. The Imm gold need to be slightly more control during reflow oven area on it's profile.
Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Wed Jun 28 16:16:09 EDT 2006 | Gman
Good article. Would EDX analysis of the cross-section at the void joints be a good method to determine any plating contamination or solder mask issues?
Electronics Forum | Mon Feb 18 15:44:49 EST 2008 | ck_the_flip
Yup! All the major players out there - KIC, Datapaq, and ECD - are all capable of profiling both reflow and wave solder. check them out. www.kicthermal.com www.ecd.com www.datapaq.com