Electronics Forum | Wed Dec 22 05:42:19 EST 1999 | Wolfgang Busko
Hi John, I�ve seen problems some sites have or had with bridging problems in the wavesolder process with 1206 and 0805. Adjusting the system and focussing on the flux parameters sometimes improved things. With some older systems it was hard to get s
Electronics Forum | Mon Dec 06 12:37:57 EST 1999 | Russ
Christopher, in response to your request concerning if I have the same issue using OA fluxes the answer would be no. This finish works well with all of our current Water Soluble fluxes. As a note, I have done some further testing and so far it see
Electronics Forum | Wed Nov 03 21:17:40 EST 1999 | Doug B.
Yes this is absolutely true. No-clean flux residue has various affects on the functionality of circuitry especially high impedance circuits. It also affects solderability, and reliability. No-clean flux will always leave a detectable residue. Mos
Electronics Forum | Wed Sep 29 07:28:04 EDT 1999 | Wolfgang Busko
3�C/min) or maximum temperature (~240-250�C)." For the correct handling of moisture sensitive devices and prebaking advices see IPC-SM-786A or newer publikations. I encountered the following: A tray of sample BGAs was send to me proper packed and se
Electronics Forum | Wed Jul 21 13:12:11 EDT 1999 | John Thorup
| I have pcb's in which i am experiencing warping. | the boards are 12.8125" on a diagonal measurement. | they are out approximatley .010". | the boards are combination thru-hole,smt, they also have 3ounce copper.what is acceptable,and what is the pr
Electronics Forum | Thu May 13 20:38:32 EDT 1999 | lima
Does anyone know of any industry guidelines for the exhausting of volatiles in reflow ovens? I've seen some numbers like 1,000ppm for the oven atmosphere, but is this typical? My concern is the volatiles in my WS629 solder paste may be attacking th
Electronics Forum | Mon Mar 01 09:49:04 EST 1999 | Justin Medernach
| It seems to be that we have to much NaCl left on our assambled PCB's. | The flux we use is from cobar. They say it can not be from the flux... So what can be the reason, what kind of problem may occer when there is to much NaCl. | George, Are you
Electronics Forum | Thu Oct 08 22:32:53 EDT 1998 | E.
*Reply to: ericr@nj.tanon.com Without going into a lengthy explaination {at this time}, has anyone experimented, tested, evaluate, and/or 'perfected' an SMT double-side reflow process. Presently I'm using a Kester R593 OA (water soluble) Sn63/Pb37 -
Electronics Forum | Wed Sep 23 15:37:58 EDT 1998 | Michael Allen
We've had success with AirVac's DRS-22 system. Their people seem to understand the rework process better than many other suppliers. I'm sure you can find them on the Web. Note: When looking at a competing supplier's equipment last year, the demo gu
Electronics Forum | Mon Jul 27 17:09:20 EDT 1998 | Rin
| We are trying to reduce the number of units fail at system test due to flux on gold finger. We know so far that the flux is deposited onto the | goldfinger during touch-up or rework and to reduce the contamination we are | planning to imp