Electronics Forum | Fri Sep 24 10:57:18 EDT 1999 | Earl Moon
| Hi Folks: | | We've been having bridging problems on our fine-pitch QFP's, despite thorough inspection of paste height, volume, and placement accuracies....profiles look good also. | | The bridging is happening after coming out of reflow...one la
Electronics Forum | Mon Apr 14 21:48:56 EDT 2008 | joseph_gonzales16
try the Orbotech SPI it is good APC is using this solder paste inspection.
Electronics Forum | Tue Oct 21 11:42:04 EDT 2008 | arosario
Hi Shooter, we're not using AOI but we do every 30 minutes sampling Inspection on the board and we're not seeing insufficient paste deposit so far since we started. But I agree with you that seemed my printer is not printing consistent amount of pa
Electronics Forum | Mon Nov 14 10:10:52 EST 2005 | davef
When soldering your full tin (no lead) and Pb95/Sn5 solder components, you need to modify your PbSn reflow recipe to compensate for the higher melting point of the changed solder alloy [with your Sn62/Pb36/Ag2 solder paste] on those component leads.
Electronics Forum | Wed Sep 15 22:52:58 EDT 2004 | pdeuel
We had same problem. Solder balls appeared on top side of board and led to damaged second side stencles. We worked around problem by running blank boards thru oven and inspecting and removing solder before processing boards with parts.
Electronics Forum | Tue Dec 23 01:23:45 EST 1997 | J.H Kim
I'd like someone gives me a tip for elemating of voids in the mico BGA solder joint and the method of inspection of them, very exactly.
Electronics Forum | Sun Jul 29 08:36:39 EDT 2001 | davef
You have provided very little information. Two similar possibilites come to mind: poor pad solderability protection and old boards. POOR SOLDERABILITY PROTECTION: Maybe the nickel plating under the gold is oxidized, contaminated, or otherwise very
Electronics Forum | Mon Dec 22 12:41:17 EST 2003 | Marc Simmel
No clean solder paste. One further observation ... the parts have a metal shell and are 'floating' high on the paste. Though there is wetting on the metal shell, it doesn't seem to sink as far as it should and this could be lifting the soldertails f
Electronics Forum | Sat Jul 28 03:05:35 EDT 2001 | Frank
Hi guy Does anyone have experiance with printing problem between solder paste water soluble 62/36/2 and gold plating PCB? I do have problem about insufficient solder after printing although I used the same printing parameter as when I print with ano
Electronics Forum | Tue Nov 02 03:24:33 EDT 2010 | Jacki
Yes, we use solder paste,solder bar and solder wire from different manufactureres for 1PCB assembly. And, what JAX said, we never mixed solder paste from different manufactures and used.