Electronics Forum | Fri Aug 13 17:53:50 EDT 2004 | masr
Any body knows where i can find some guidelines for solder paste printing or most recomended paste parameters? Thanks in advanced!
Electronics Forum | Wed Apr 18 08:57:45 EDT 2018 | davef
Here is the IPC Standards Tree [ http://www.ipc.org/4.0_Knowledge/4.1_Standards/SpecTree.pdf ]. The design standards that you ask about are over on the right side. I'd guess that the following standards would be a good starting point: * IPC-2221, "
Electronics Forum | Wed Jun 05 15:22:48 EDT 2013 | davef
Solders, Fluxes and Pastes - A Lab Report This webcast consists of 10 individual program segments focused on the important topic of electronics solders, solder pastes and fluxes. Program Segments Include: * Can You Mix Leaded and Lead-free? * Probl
Electronics Forum | Fri Mar 23 03:41:19 EDT 2012 | grahamcooper22
try Almit Sn62 HM1 RMA V14L ....its the best no clean lead paste for wetting...I sell it and it has solved wetting problems many times when users have used other pastes
Electronics Forum | Tue Jan 31 10:59:55 EST 2006 | carterhoward
Hi All, I�ve been doing some research on the issue of running lead-free solder paste and leaded solder paste through reflow at the same time. The point with this would be to process all standard leaded components with Lead paste while also processi
Electronics Forum | Thu Nov 08 10:52:22 EST 2012 | Bryan Ng
I am considering using high-temp ball Sn10Pb90 + eutectic solder paste for MLC reflow (no underfill). You can see that there is no Intermetallic bond for the paste and the balls. Under high stress/shock condition, the solder joints develop micro c
Electronics Forum | Mon May 27 11:13:11 EDT 2013 | ericrr
Is there any good articles to read on solder paste? (just to see if I may of missed something) Sometimes I can not believe the people I have to work with. We had a panel with two “Quad Flat Package” (QFP) one in each of the two circuits, almost fr
Electronics Forum | Sat Sep 12 10:12:20 EDT 2009 | tylaburg
My customer wants an SnPb 63/37 BGA soldered using SAC305 solder paste. What data is avaiable showing the long term reliability of the intermetallics of the solder joints?
Electronics Forum | Fri Mar 23 10:00:38 EDT 2012 | isd_jwendell
I am a big fan of AIM SnPb solder paste. I currently use NC257-2 (no-clean, 89.5%), and recommend you include it in your evaluations.
Electronics Forum | Thu May 30 09:14:03 EDT 2013 | emeto
I have another idea. Would you check the apertures on the stencil? May be they didn't cut the right size apertures there. If you have smaller aperture you can't get the right amount of paste.