Electronics Forum | Wed Apr 28 16:41:52 EDT 1999 | KH (factor)
| Anyone using hot air nife for wave soldering process. | Does it work? | Does it really eliminate solder bridging and does it create any other problems? | | any feed back will be much appriciated. | | Thanks | | Tony A Hi Tony I have bought a
Electronics Forum | Tue Nov 11 16:07:52 EST 2003 | johnwnz
Folks, has anyone heard fo any problems with RF cards related to solder paste selection. Currently runnign with std SnPb paste but want to move to 2% silver paste. Was asked if this could cause any issues in term's of RF capability or interferance t
Electronics Forum | Tue May 25 10:16:03 EDT 2004 | Bimal Patel
We are doing assemblies using Immersion Silver coating for RF assembly for a while now. We did not have problem using 63/37 SN/PB solder paste untill recently. We started seeing black marks on the finish and around the solder joint recently. We have
Electronics Forum | Tue May 25 10:16:07 EDT 2004 | Bimal Patel
We are doing assemblies using Immersion Silver coating for RF assembly for a while now. We did not have problem using 63/37 SN/PB solder paste untill recently. We started seeing black marks on the finish and around the solder joint recently. We have
Electronics Forum | Mon May 20 15:43:01 EDT 2013 | ngotranbestek
Hi I meet problem by PCB with diameter 300cm and thick 6mm i used tin-lead with profile normal, soak time 60-90 sec, Temp peak is 220 degree C, But solder see not good, not shiny. Any body recomend help me to fix this problem for Hard gold playing.
Electronics Forum | Fri Jun 09 20:13:36 EDT 2006 | grantp
Hi, We have spent the day trying to profile our Vitroncis Soltec Delta C wave with the new SN100C solder, but having problems with the heavy pins on some BNC connectors we are using. We have Interflux no residue flux, and we are using palettes, whi
Electronics Forum | Wed Sep 20 15:51:19 EDT 2000 | John
We are considering retrofitting our Vectra wave soldering machine with a hot air knife. I've run our problem board on a machine with this option and it does seem to work; however, there is a concern of component failure due to thermal shock. Is thi
Electronics Forum | Mon May 07 18:30:23 EDT 2001 | genny
If a PCB is already going through ICT and some additional inspection method is desired to increase first pass test yield rates, what are the advantages/disadvantages of AOI vs XRay? The most common problems seen are missing or skewed components and
Electronics Forum | Mon Jun 18 16:13:47 EDT 2001 | calipso
If a PCB is already going through ICT and some additional inspection method is desired to increase first pass test yield rates, what are the advantages/disadvantages of AOI vs XRay? The most common problems seen are missing or skewed components and i
Electronics Forum | Wed May 07 15:36:04 EDT 2008 | llaerum
The 483 is what we use on all boards except on one where the 353 improved wetting on resistor packs. It worked much better since the parts are LF and this is the same flux AIM uses in their LF solder. Yes, it was recommended by AIM when we discussed