Electronics Forum | Wed Jul 24 11:46:58 EDT 2002 | johnw
Claude, your not a manager by any chance are you?... you can't charge them for breaking them. Ok so yes there will be poor handling but if your going to fix the problem you have to look at teh route cause of it and fix that. You should be settign up
Electronics Forum | Tue Jan 28 18:38:36 EST 2003 | joeherz
Mike, I've tried the high side of the flux preheat spec with no success. I did just get off the phone with Electrovert tech support...... Get ready. This machine is configured with a Contour Plus N2 nozzle. We are not running N2. According to M
Electronics Forum | Thu Sep 18 15:29:59 EDT 2003 | Gabriele
Hi all, by reading along those thread (SOT23) and Tan outgassing I learned plenty of things. My first time approacing this kind of Q$A Forum, very intesting tech communication way. Any way, the path of magnetism effect was chosen when time ago we met
Electronics Forum | Tue Jul 20 12:49:38 EDT 2004 | mmjm_1099
We are having a problem with our Heller 1800W oven with certian parts skewing. It seems that some inductors and taller Can caps are shifting around in the oven. It seems it will solder fine and than all of a sudden just be off to one side or the othe
Electronics Forum | Fri Jul 01 18:00:44 EDT 2005 | mrduckmann2000
RB, We have a gold finger problem here at our plant. Our kapton tape came off in the wave process and now we have 8 PCB's that have silver fingers. We are waiting on our new A.P.E. SRS-069 Gold Finger Plater. This mircle machine is going to fix a
Electronics Forum | Fri Jul 15 13:28:55 EDT 2005 | Brian
A process consists of much more than just thee machine. When developing a cause and effect diagram ffor the process, there are many parameters that fall outside the machine itself. There are Man, Machine, Methods, and Materials. Just monitoring th
Electronics Forum | Tue May 02 16:21:05 EDT 2006 | patrickbruneel
Grant, I personally disagree that lead-free can't be reversed. The reason it went that far is because lead has a bad reputation (lead in gas and in paint)and was probably assumed by the European green politicians as equally bad in solders. When they
Electronics Forum | Thu May 11 13:28:49 EDT 2006 | patrickbruneel
Being a typically efficient Swiss based company Swatch started the task of RoHS conversion a year ago. After 2 years of intensive research they implemented the process in mass production in June 2005, they started shipping and found massive problem
Electronics Forum | Tue May 30 08:46:10 EDT 2006 | patrickbruneel
Interesting read, I guess they finally figured it out (with 32 days left) 2 quotes from the articles "What is surprising however � although it should not be � is that, despite the claims of health and environmental threats, the latter based on the r
Electronics Forum | Thu Jan 04 17:04:43 EST 2007 | slthomas
99% good solder joints = 10000 ppm (defects per million opportunities). Having only built with 0603s I can't speak for a target but that still seems pretty harsh....with a 75/25 0805/0603 ratio at my last place of employment I think we were running