Electronics Forum | Tue Jul 04 16:13:09 EDT 2000 | TOOLMANTIM
HELLO BILL I HAVE SOME QUESTIONS FOR YOU 1:HOW ARE YOU CLEANING YOUR STENCIL 2:ARE YOU SINGLE OR DOUBLE PRINTING. 3:ARE YOU USEING VACUUM FIXTURES OR NOT? HERE ARE SOME OTHER THINGS TO TRY. IF YOU ARE CLEANING YOUR STENCIL OFTEN BECAREFUL OF USEING
Electronics Forum | Thu Jun 22 12:06:10 EDT 2000 | Wolfgang Busko
Hi Sal, I assume your homeplates are designed with the peaks towards the componentcenter. I can imagine that due to placement inaccuracy not both sides sit in the same amount of paste and that wetting difficulties prevent same force factors for both
Electronics Forum | Wed Jun 21 05:14:49 EDT 2000 | Wolfgang Busko
Hi Ivan, J-STD-001C chapter 3.6.2 says temperature should be maintained between 18�C and 30�C and humidity should not exceed 70% and below 30% verification of electrostatic discharge control is advised. This is a wide range and I wouldn�t allow a sw
Electronics Forum | Thu Jun 15 22:06:15 EDT 2000 | Dreamsniper
Hi Raeto, 1. You do not have reflow oven. This means that you are not running Surface Mount Technology in your shop floor...am I correct? Why do you plan to have SMD's under your PCB's ? Can't you replace them with their PTH counter part and have th
Electronics Forum | Wed Jun 07 12:11:42 EDT 2000 | Rex Breunsbach
First of all I would like to thank you for your candid comments on this subject. ECD listens to its customers and values their input. Yes, our experience shows the coupons have a 30 to 60 run life depending on application. This works out to between
Electronics Forum | Fri Jun 02 09:31:26 EDT 2000 | C.K.
Okay, there's a debate here at my company. We build a card here that, often times, we get batches where there is excess HASL in the VIA hole barrels. Here is the problem that this causes: During the "1st reflow", the excess HASL bleeds out of the
Electronics Forum | Mon May 22 12:04:03 EDT 2000 | Michael Parker
80%. There are too many factors at hand to point the finger yet. We need to build a truth table and dot the i's and cross the t's before stepping up to Goliath (Samsung). Is you placement guranteed good? What x-ray have you used? Are your fab.'s know
Electronics Forum | Mon May 22 16:50:50 EDT 2000 | Kathy Palumbo
Mike, Is that greater than 80% yeilds, or less than? Here are the answers to your questions: Is you placement guranteed good? YES What x-ray have you used? Nicolet Are your fab.'s known good? YES Could you de-solder Samsung and replace with ano
Electronics Forum | Tue May 16 22:59:37 EDT 2000 | Dave F
How do you control the "lost" of dross dust in you collection can? When picking dross from our wave; we gear-up, hook-up an aux vent pipe, and use ss kitchen utensils to seperate the dross from the solder mass. We deposite the dross into a 5 gal co
Electronics Forum | Wed May 17 23:02:25 EDT 2000 | ScottM
We don't do any of this. We had our operators tested by OSHA for lead inhalation using special sniffers during the wave solder process and passed by a magnatudes in limits while operating the machine and removing dross. Our recycling agency doesn't