Electronics Forum | Tue Dec 03 15:26:07 EST 2002 | GSW
This might be a trival mundane suggestion but try to use non conductive plate to hold components. Probably even made of the pallet material. I am sure your pallet fabricator will have tons of scrap and he can help you find one. T
Electronics Forum | Tue Dec 03 11:59:01 EST 2002 | slthomas
We haven't run a profile yet....probably because we're a-feared to. We can't do topside preheating here to any degree because we use an aluminum plate for aligning hundreds of top side through-hole components (pots, switches, buttons, LEDs) that te
Electronics Forum | Tue Dec 17 13:42:04 EST 2002 | robf
There are a few emerging technologies that have been growing in popularity for the past few years. Pin through paste, press fit connectors and selective soldering machines seem to be displacing custom fixtures. Most of the mixed technology boards o
Electronics Forum | Mon Dec 16 19:05:57 EST 2002 | davidduke
Steve , I agree with all the responses you have received. Randy Villeneuve is absolutly correct in all of his assesments and I would consider him an expert with the process , Gris is correct about adding a "heat sink" to the process complicating pr
Electronics Forum | Tue Dec 10 14:10:38 EST 2002 | Randy Villeneuve
Steve, I wave solder most if not all our boards with selective wave pallets. I did not catch if the solder balls were on top of the board or on the bottom but that will make a difference on what to do to get rid of them. Pallets are good and bad. On
Electronics Forum | Mon Jul 12 21:05:06 EDT 1999 | karlin
Hi, I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) Secondly, I need also facing a lo
Electronics Forum | Tue Sep 17 15:47:42 EDT 2002 | stepheno
Where I worked previously we had some boards with a couple 15 mil pitch parts. The first batch we got all had undersized pads. We had lots of bridging. We had less bridging with bigger pads. The ball size in the paste makes a bigger diffence regar
Electronics Forum | Tue Feb 06 21:43:11 EST 2007 | Wayne
If it is instructed to ship lead free product to customer, then low temp lead free solder paste can be considered. For example, Viromet solder paste from Singapore Asahi (peak temp is between 220 to 225 degree C).
Electronics Forum | Mon Feb 05 21:56:31 EST 2007 | ViVian
what type of solder paste I should use if Rohs and non rohs component mount on same board
Electronics Forum | Tue Feb 06 06:41:53 EST 2007 | pavel_murtishev
Good afternoon, You have to use lead paste since none-RoHS components won�t withstand elevated temperatures. Solder paste manufacturers offer a lot of transitional pastes designed specially for mixed process. Ask your paste supplier for transitional