Hi, I have a lot of solder bridge in our wave soldering process.We use SACX0307 and Surf 11 flux.the SW mashine is Vitronics delta 6622.Itry to change flux and termoprofile but results is not god.Can you halp me - recommend me some flux or other adv
Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc
5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht
Electronics Forum | Thu Jun 22 15:05:55 EDT 2017 | solderingpro
There are several different technologies in the industry today to assist in the out-gassing of flux cores. On automated soldering systems, there are two main types of perforating solder feeders: - Hole Drilling - "V" Scoring By perforating the so
Electronics Forum | Tue Feb 29 21:53:46 EST 2000 | Kelvin Chow
Dear Robert, On PBGA assembly, BGA sphere shrinkage number depends to the following factors, a. BGA Sphere size (before reflow) b. Solder mask opening diameter As far as I know, no formular has been established yet. Most of my friends just collect
Electronics Forum | Tue Feb 29 21:53:46 EST 2000 | Kelvin Chow
Dear Robert, On PBGA assembly, BGA sphere shrinkage number depends to the following factors, a. BGA Sphere size (before reflow) b. Solder mask opening diameter As far as I know, no formular has been established yet. Most of my friends just collect
Electronics Forum | Mon Nov 21 06:49:57 EST 2005 | pjc
Go to this link for a nice tool for wave solder process troubleshooting: http://www.speedlinetech.com/news_publications/application-notes.aspx?OnId=5 Look for "Wave Solder Troubleshooting Wizard" If you have an Electrovert machine, contact applica
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Thu Nov 17 21:46:48 EST 2005 | C. Kolokoy
With DIP type components, a sub-par fluxing method (foaming a no-clean), and a chip wave where one is not needed are formulas for bridging and insufficient wetting. If you have SMD's on the wave solder side of the board greater than 0603, and no SOT
Electronics Forum | Fri May 15 21:39:48 EDT 2015 | jlawson
Reflow.. 1.Rehm (Germany) - Best in Class Best overall process stability heating system ( Alot of makers have started to copy there VX heating arrangement ). COnveyor chains can be a bit more attention in terms of maintenance on rehm , but if foll
Electronics Forum | Tue Jan 31 12:13:26 EST 2006 | Calvin Kolokoy
Today's regular Sn-Pb paste chemistries are designed to run at higher peak temperatures ensuring that your lead-free alloys will coalesce with your regular Sn-Pb solder. That being said, it is do-able to solder both types in one oven. Generally, wit