Electronics Forum | Tue Feb 15 14:35:41 EST 2000 | Balas
hi I am designing a test vehicle with a range of components on it(pbga, cbga,fc, mbga, and qfps). My concern is that I would like to use a single stencil for solder deposition and not a stepped stencil. That would require me to have aperture design a
Electronics Forum | Thu Apr 26 12:06:08 EDT 2007 | basem
$100K for this entire line. We are thinking of getting a Chinese made reflow oven that looks pretty good at $25K. Also, we need to deposit solder using a dispenser as stencil printing will be reserved only for higher volume boards. It will not be pra
Electronics Forum | Mon Nov 15 12:09:55 EST 1999 | Dave F
Steve: Continuing with Dan�s thinking, generally, "poor release" (paste hanging-up in the stencil holes) could have three main (or combination of) causes: 1 Equipment: Stencil is too thick. Specifically, your 0.006 should be OK, providing you don�
Electronics Forum | Fri Sep 21 01:31:13 EDT 2001 | Stoney Tsai
Guys, If there are any specifications or ciriterions for solder paste deposition thickness and volume evaluation. For example, QFP (0.5 mm pitch), 6~8 mils, 3000 mil^3 PLCC: 8~10 mils, ... . . Thanks in advance. Best Regards,
Electronics Forum | Sat Nov 13 14:09:45 EST 1999 | se
First, let me say what I always say: a good chem-etched stencil will print fine pitch. Chem-etch brings trap to the side walls because its a physical by-product of the process. Because they are less expensive you can add electropolish and still save
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Wed Mar 01 16:59:44 EST 2000 | Dave F
Robert: Expect a 0.033" raw ball to be within 0.022" of the pad, after reflow. To be clear, that�s not a matter of shrinking by 33%. The volume of solder on the pad is the same as the volume of solder in the raw ball. It�s just that the solder is
Electronics Forum | Wed Mar 01 16:59:44 EST 2000 | Dave F
Robert: Expect a 0.033" raw ball to be within 0.022" of the pad, after reflow. To be clear, that�s not a matter of shrinking by 33%. The volume of solder on the pad is the same as the volume of solder in the raw ball. It�s just that the solder is
Electronics Forum | Thu Oct 02 01:47:57 EDT 2008 | myleb
I'm new to SMT. Now, i'm making program for SPI machine to inscpect for solder paste of SP60-MU. I think this is a very good printer but some times, my program shows only 50-60% of volume transfer; and the average height is very high: nearly 200 pct.