Electronics Forum | Thu Oct 28 13:36:14 EDT 1999 | Bart Smith
I am a design engineer and have a circuit board design with a 292 pin BGA on it. The board manufacturer is experiencing a failure rate of about 2.8% on the BGA device due to soldering problems. This is my first experience with BGA. How does the 2.
Electronics Forum | Fri Oct 29 05:23:00 EDT 1999 | Wolfgang Busko
Hi Bart, that�s much to high. If that would happen to me my boss would tear my head off. For improving the yields you must find the cause for the soldering problems. What are the symptoms? What could be the cause for the symptoms? Could be design pr
Electronics Forum | Tue Feb 08 04:27:55 EST 2011 | thomas111
hi, I am a Hardware designer . One of my products is undergoing a Reliability test in which a resistor shows a high value on board from its specified value .However it retains the original value when its cooled under room temperature. The resistor
Electronics Forum | Tue Sep 26 18:06:13 EDT 2006 | russ
could be black pad, or it is just bad reflow profile that did not get all balls soldered down. OR it could be a planarity issue between BGA and fab during assembly. Can we assume that this is proven design? Somewtimes in new design touching a BGA
Electronics Forum | Tue May 06 15:09:33 EDT 2003 | russ
Is that coating pliable? How is it cured? Russ
Electronics Forum | Thu May 01 20:40:15 EDT 2003 | davef
Are you talking to these guys? http://www.smtnet.com/Forums/Index.cfm?CFApp=1&Message_ID=24298
Electronics Forum | Tue May 06 15:53:52 EDT 2003 | bremerg
The coating is pliable and is air cured for 24 hours. The potting compound goes into the top assemnbly in 3 diferent stages. The circuit boards are coated using urethane type conformal coating. The unit is also placed into an ESS chamber -40� to +
Electronics Forum | Tue May 06 14:52:37 EDT 2003 | bremerg
Pictures are now located at http://www.stevezeva.homestead.com/ These components are 2W resistors that only see 1/2W at max. during normal use. I have contacted IRC still wqaiting for a response. The resistors were tested as good. But the circuit
Electronics Forum | Thu May 01 13:58:14 EDT 2003 | bremerg
Gentlemen, Does anyone have any failure information on IRC, CHP2-100-R500F (5 OHM, 2W, 1%) resistors. We have experienced two failures on the same circuit board where the metalization on the component separated from the component causing an open ci
Electronics Forum | Thu May 08 10:16:17 EDT 2003 | davef
Observations are: * Center most lead of the fuse on the top right of the assembly looks like it has excellent solder flow, but this is PTH. From the amount of solder, it must have been wave or hand soldered. * Center most lead of the fuse on the bot
winsouce.jpg)