Electronics Forum | Wed Jul 09 16:00:04 EDT 2008 | grics
Obviously you wouldnt perform the most difficult rework tasks till last... Sorry. I should have clarified. We rack our units to keep good units flowing and fall out are held for rework. The line never stops. Inspection is inline and it is the deci
Electronics Forum | Fri Oct 17 14:55:50 EDT 2008 | rway
We use a YesTech M1 system. I have been pleased with it's performance and feel it has done fairly well being that it only has one vertical camera. There are different algorithms you can use to compensate for the lack of angled cameras to catch some
Electronics Forum | Wed Feb 04 03:20:05 EST 2009 | smartasp
Hi All Reflow Gurus I have learnt that my process engineers do not consider the heat resistance, of the components when creating a reflow profile but rather try to stick to the paste recommendation. This has lead to a field recall as one component h
Electronics Forum | Fri Sep 04 02:09:03 EDT 2009 | sachu_70
Hi Walter, Do you refer to a sprayfluxer operation? The problem seems to be a parameter setting issue. 1. Ensure the wide angle spray reaches PCB with optimum jet pressure. You could pass a glass plate to understand flux coverage and view Jet pressur
Electronics Forum | Mon Dec 28 09:12:56 EST 2009 | kpm135
@tommyg_fla According to the TDS the recommended coating thickness for Humiseal 1B31 is only 1-3 mils so if I had to guess I would say your issue might be that you're re-coating over the first pass too soon. All the solvent hasn't evaporated and the
Electronics Forum | Tue Mar 23 15:46:28 EDT 2010 | pilusa
The AIM flux is for the process and not for the tip tinning. The flux I was referring to is what is used to keep the tip wetted which was one of your original problems. Regarding the process, in my experience the AIM flux is not very active and there
Electronics Forum | Wed Jun 08 13:49:48 EDT 2011 | sonofptolemy
Hello, I am having a problem with HASL PCB's after it comes back from the stuffer. To me it looks like oxidation and it causes poor wetting. This leads to a bunch of problems all of which have different symptoms but the cause is this oxidation proble
Electronics Forum | Fri Aug 31 13:51:33 EDT 2012 | joeherz
First off - There should be no issue with washing your OA/water soluble boards with the other customer's no clean units provided that the recipe being used has been validated to effectively clean each product. If your supplier is using a batch syste
Electronics Forum | Wed Jun 12 14:42:40 EDT 2013 | armandogomez
Hello guys ! I am here again with a problem, right now we have a problem with a new product, the problems are with voids with the PTH we put a receptacle with terminal blades that are 1.3mm width in a pth with a diameter of 1.5mm we use a pallet to
Electronics Forum | Wed Jul 03 14:16:09 EDT 2013 | horchak
Hi, I had seen your post earlier but had lost my very old log on information. First I will say that BGAs should never be placed and re-flowed with a rework station unless there is absolutely no other option, so I don't understand why your assembly ho