Electronics Forum | Fri Nov 06 11:56:43 EST 2015 | derrikf
They're probably 12 - 18 inches, maybe slightly longer.
Electronics Forum | Wed Sep 10 14:56:57 EDT 2008 | rarnold
I am dealing with a similar uncoalesced solder issue. This defect has come and gone several times during the last 6 months. See image. In my case, I am using conventional SnPb solder and an entire strip of my OSP finished board (includes various de
Electronics Forum | Thu Oct 23 11:23:46 EDT 2008 | muarty
Our solder bar supplier provides this service free of charge. I also use an independant lab in the UK for testing too. Well solder suppliers are hardly going to tell you that you have an issue with solder they supplied are they..........?
Electronics Forum | Wed Dec 10 09:29:59 EST 2008 | rgduval
Oops...just noticed you were referring to wave soldering. We'd still suggest a water-soluble flux, instead of the no-clean; especially at wave soldering. Also, checking pre-heat temps, and dwell time on the pot. Is the wave a chipper wave? If not
Electronics Forum | Tue Sep 02 15:40:58 EDT 2008 | bvdl
use the 2009MLF from Interflux it will take away your solder balls. this is a known issue.
Electronics Forum | Wed Mar 05 08:12:56 EST 2003 | nifhail
Hi Mike, How do we measure the O2 ppm in N2 environment. I don't understand why the customer keep insisting me to use N2 instead of Air. I don't see the need for it as I done have any soldering issue. Can you share with me why N2 is needed at the fi
Electronics Forum | Fri May 06 06:51:55 EDT 2016 | abhilash4788
Hi All, One of my customer has provided a pcb design having common pad for 0402 and 1206 package(i.e 3 pads in the gerber, pad1,pad2 belongs to 1206 package and pad2,pad3 belongs to 0402 package) Will this create any solderability issue. Is anyone e
Electronics Forum | Mon May 06 11:49:20 EDT 2002 | Jacob
Hello all, I am having soldering issues with an Everlight component it is a TM4201/TR2 (Right angle IRDA with a 1mm pitch). The problem I have is that after reflow the solder joints look perfect, but during test we are losing 7 micro amps as soon as
Electronics Forum | Tue Apr 17 10:22:16 EDT 2001 | tom g
Has anyone out there had solder joint wetting issues with Murata ceramic chip caps, in particular with Alpha UP78 no-clean paste? We are finding that changing either the paste or the vendor corrects this problem. If so, please advise your solution(
Electronics Forum | Mon Nov 12 01:18:29 EST 2007 | sin4d
Hi, ALL I experience some QFP with wetting issue on the heel of the lead. There is no fillet wetting on the heel which causes reject bt the customer, but not all the QFP. Could anyone pls help what is the causes of this problem, it is due to oxidati