Electronics Forum | Tue Apr 13 08:08:33 EDT 1999 | Rob Palson
We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to bu
Electronics Forum | Mon Apr 19 02:38:41 EDT 1999 | Brian Sloth Bentzen
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Mon Mar 29 04:00:01 EST 1999 | Vinesh Gandhi
Glenn, i am aware of one unique problem with voc free fluxes. since these fluxes have certain amountb of water content they cause sputtering leading to solder balls & voids problems. Regards Vinesh Gandhi | I require some feed back from any one
Electronics Forum | Thu Mar 11 01:54:55 EST 1999 | Marcus Reichenberger
Hello everyone, at the Institute for Manufacturing Automation and Production Systems of the University of Erlangen (Germany) one focus of our research activities is the use of lead-free solder alloys for electronics production. In different publicat
Electronics Forum | Tue Mar 02 23:08:54 EST 1999 | Marsellus Wallace
| Hello, | I'm doing some research for a project of mine. | I figured that since you sold things related to soldering, | you might know. | | I am wondering if there are any companies that | you know of that do manual soldering while st
Electronics Forum | Mon Feb 15 15:43:06 EST 1999 | Dave Jurena
Hope some of you out there can help me with this one. I am getting feedback from our test department that they are showing opens on solder joints which have visually good wetting. The touch-up operators confirm that the joint looks good. All they do
Electronics Forum | Wed Jan 27 19:42:34 EST 1999 | parag palshikar
i am working with the noclean process and getting white residues on the bottomside of the board probably due to the wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated temperature a
Electronics Forum | Wed Jan 27 11:42:50 EST 1999 | John Zisa
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Thu Jan 14 21:24:35 EST 1999 | Bernie
Due to an foul up on my part, a circuit board ECO snuck up on me and I have a solder paste stencil that doesn't quite match the board. Two pads are off by about half a pad each. Can the solder paste stencil be modified? If so, what is the technique
Electronics Forum | Wed Jan 20 22:46:44 EST 1999 | Bernie
Thanks for the info. I modified the stencil, ran the boards, and just got a new stencil. Life is good again. Bernie | Due to an foul up on my part, a circuit board ECO snuck up on me and I have a solder paste stencil that doesn't quite match the boa