Electronics Forum | Mon Jun 20 21:54:38 EDT 2005 | darby
Contact your paste supplier and see what they say. My information on SAC 305 FROM MY SUPPLIER was - "The cool down rate is not as critical for Pb-free solder joints, as it was for SnPb. The grain sizes do not differ is size in the Pb-free bulk solde
Electronics Forum | Wed Jun 29 17:38:16 EDT 2005 | GS
Several years ago, we had almost same pbm, best results have been obtained by using water soluble paste (those time the old AM1208). Any way, to get a good toe meniscus is not so easy. Talking about CTE, keep in consideration the internal die of TSO
Electronics Forum | Tue Jun 28 10:51:32 EDT 2005 | mattkehoe
Thanks for the replies, - solder paste used ? NC ? other ? Water soluble 63/37 paste - reflow in Air or N2 ? Infrared - temp ramp up before soack (�C/second) ? Will have to check. This profile has been used on numerous gold plated boards in our
Electronics Forum | Fri Jul 08 10:08:12 EDT 2005 | fctassembly
Dear Hiram, Thanks for your interest in SN100C. FCT Assembly is a licensed manufacturer of SN100C from Nihon Superior for North America. We have the alloy in 5 application labs- FCT (CO), Vitronics (NH), Technical Devices (CA), Electrovert (MO), and
Electronics Forum | Wed Aug 10 21:47:17 EDT 2005 | Geoff
Nihon superior could not provide any written aprovals but In asia.......... Sony- SN100C in use for car and home audio applications. Panasonic- SN100C in use for DVD, VCR, battery, and home appliances applications. Pioneer- SN100C in use for everythi
Electronics Forum | Tue Jul 05 10:04:59 EDT 2005 | Inds
Hi All, we are running a process where we are wave soldering the PTH components using SAC305 alloy. During rework process (using SAC alloy in the solder pot) we are seeing good amount of Cu dissolution, to an extent that the Cu has completely disapp
Electronics Forum | Thu May 25 08:47:39 EDT 2006 | inds
Patrick, we were seeing a good amount of Cu-dissolution with both SAC305 and SN100C.. couldn't figure out.. till our good old vendors told us that the Cu thickness in the barrel were not correct... but anyway have started some new work with SAC30
Electronics Forum | Thu Jul 07 18:16:36 EDT 2005 | russ
What size discrete components and have you evaluated your pad geometries? If pads are too far apart this will happen. The flux resudue is simply there because you didn't solder the component. It will stay on top of the solder bump. You can see this
Electronics Forum | Thu Aug 04 12:40:38 EDT 2005 | Ted
Hi all, I am wondering what everyone is using as a PCB finish for RoHS. There doesn't seem to be a favorite out there. I know there are many companies using a gold finish but I don't want to pay that much and I have also heard about reliability p
Electronics Forum | Thu Aug 11 03:56:11 EDT 2005 | md
Guys, I have a 2.4mm pcb 8layer with a lot of copper on board. I am having some problems with solder not travelling up through the holes. Looking from the bottom of the board it looks fine . Also, To measure temp. of board through preheat zones