Electronics Forum | Mon Jul 07 21:33:15 EDT 2014 | andrespena
The problem about covering it with glue (without using solder) is that the components might dislodge by a miniscule amount underneath the glue. So maybe the contact points will disconnect. I'm not sure if this will be a real problem, but if so it wo
Electronics Forum | Thu Jul 17 20:20:21 EDT 2014 | mac5
Hi June, The biggest issue with an OSP finish is as soon as the PCB sees a heat cycle (reflow or wave) the finish will begin to degrade. If you have a single sided SMT assembly with THT components installed downstream it works pretty good. But a dou
Electronics Forum | Mon Aug 04 08:33:45 EDT 2014 | emeto
I worked with a few BGA rework stations and also had the chance to see several demos on different brands. THe good ones that can really do it are equipped with camera, infrared under the board, different nozzles and a hot air comming from the head(di
Electronics Forum | Fri Oct 10 20:56:50 EDT 2014 | jlawson
Main issues... Pad Design Thermal Mismatch Design related to pads effected Moisture and out gassing in substrate / part terminations can move parts slightly during preheat prior to liquidous this get position shift ( smaller the parts more an issue)
Electronics Forum | Tue Oct 21 22:25:35 EDT 2014 | richardciccarone
Thanks for the input. I read that paper. I'm not convinced the Pb stabilizer and bath MTO's are a cause of the Black Tar defect. If that were the case, given the history of Pb stabilizers and ENIG, I would have thought that there would have been many
Electronics Forum | Sat Oct 25 13:36:39 EDT 2014 | sonavc
Hi everyone, hope you can help me with this machine I bought used and after it is set up , it runs good, home position. I can click the tab Start, and Setup. But I can't click the tab I/O , edit or system. Because, I think I can't log in the Level
Electronics Forum | Tue Nov 04 12:10:56 EST 2014 | richearle
Hi, I've got a Microline 200TF - I guess it's a 1980's machine. It's gone pop and I cant fix it without a circuit diagram (there's several pcbs in it with a variety of relays, triacs and what-not). If anybody has a circuit or any othe rinfo on it I
Electronics Forum | Fri Nov 14 10:45:22 EST 2014 | tombstonesmt
We use both types in house. We started with a board moving over the pot, slowly moved on to Jade machines and eventually Synchrodex. Like you mentioned without palletizing you'll have component movements during the cylce and most likely won't have th
Electronics Forum | Thu Nov 20 18:57:52 EST 2014 | warwolf
I can only say it looks okay for what you need, you will want a dual wave system it can make things so much easier. One thing to check would be the wave nozzle sizes I can see that the conveyor will do up to 15" but thats not to say the nozzle is
Electronics Forum | Mon Dec 22 18:20:22 EST 2014 | sreejhu
Hello, Also I wanted to tell you. I decided to go with a brand new machine. Please tell me which is the best machine for mid Volume. Samsung, heller, Dima, essemtec, acto USA, C.I.F Which company do you suggest me.. The best. My duties: We have boa