Electronics Forum | Fri Dec 26 00:30:36 EST 2003 | Indy
hi, I wondering if anyone have any information on intermetallic growth in 80Au20Sn solder alloy. I have read that it has high reliability. Which bring an important question to my mind. What about Gold embrittlement ? Bye Indy
Electronics Forum | Tue Dec 30 21:14:22 EST 2003 | davef
You're thinking correctly. 80Au20Sn is incompatible with: * Sn/Pb * In/Sn * Sn/Pb/In * Sn/Pb/Bi Contact your solder supplier to obtain pictures of IMC.
Electronics Forum | Fri Jan 02 11:30:54 EST 2004 | JG
We purchased this wave solder machine used. It came without the operating software (TECDEV). I want to know how to adjust the temperature deviation setpoint. Does anyone know how to do this? Thanks in advance, JG
Electronics Forum | Tue Jan 06 19:53:32 EST 2004 | jj
Hi, Any idea what's the possible causes of cold solder after drop test? Thanks JJ
Electronics Forum | Tue Jan 13 09:38:52 EST 2004 | mleber
Can anyone provide a list of the top 5 solder paste / wave flux manufacturers by sales? We are evaluating changing to a new chemistry and would like evaluate several of the top manufacturers. Thanks.
Electronics Forum | Fri Jan 16 15:07:45 EST 2004 | Phil
I have a connector which has very weak joints. Solder fractures easily. On inspection the solder is very grainy and full of voids. Process is 63/37 no clean. Any thoughts? Phil
Electronics Forum | Tue Jan 20 21:37:26 EST 2004 | alwil
I am looking for a supplier or a manufacturer who can help me with Titanium Fingers for our Electrovert Econopak Plus wave solder. I am looking for the "v" groove type and also the 90 degree type fingers. I am in Australia. Thanks.
Electronics Forum | Mon Jan 26 11:41:04 EST 2004 | pbarton
Some questions: Is the peelable/spot masking only being applied to the earthing points on the one side or to both sides? Is the peelable mask you are using specifically designed for coating masking or is it the same as that you use for masking sold
Electronics Forum | Wed Jan 28 14:35:12 EST 2004 | swagner
Has anyone in the industry had even a fair amount of success inspecting reflowed solder joints to IPC class 3 standards? I am not interested in hearing from system reps or people who work for an AOI manufacturer. Thanks,
Electronics Forum | Mon Feb 02 12:36:41 EST 2004 | paul_bmc
90% of the assemblies our company produces are class 3 and we have no problem at all inspecting or getting class 3 quality through reflow. Rarely do we have touch up because of insufficient or poorly reflowed solder joints. What are the problems you