Electronics Forum: soldering temperature fr4 (Page 1 of 230)

Re: temperature range

Electronics Forum | Mon Nov 27 17:44:10 EST 2000 | Dave F

Gawd. Sure FR-4 will meet those conditions. Tg [check the fine SMTnet Archives for discussion on Tg] of FR-4 is 130�F or so. Consider: * Is the delT between Tg and the upper operating [or storage] temperature acceptable for your application? * D

Wave soldering temperature

Electronics Forum | Thu Nov 04 11:56:33 EST 1999 | Tim Almy

Is 260 degrees C / 500 degrees F the optimum temperature for wave soldering ?

Wave soldering preheat temperature

Electronics Forum | Mon Apr 16 12:59:51 EDT 2001 | Mike R

If you will place a temperature strip on the board during wave soldering process you will get a max of 210 F or 98.8 C which is normal on the standard wave temperature. The problem on the 10% solder on the TH via hole can be caused by insufficient fl

High temperature soldering

Electronics Forum | Fri Apr 24 14:34:14 EDT 1998 | Ed Holton

Looking for anyone who has experience with high temperature soldering. Need to determine why solder joints are failing. Thermocycling of unit is -40C to +140C, 30 minute dwell time, 10 sec. transition time Your help is appreciated Ed Holton Hella E

reflow / soldering temperature

Electronics Forum | Thu Apr 05 10:50:08 EDT 2001 | CAL

Per our staff here at ACI......... Higher Temperatures maybe necessary to achieve good solder process results. The alloy formed when HASL coating protects the copper is the same as that when OSP provide protection. Temperatures may be increased to im

Re: Wave soldering temperature

Electronics Forum | Thu Nov 04 15:57:46 EST 1999 | Dave F

I'm with John. Back in the old MIL-2000 days, the pot temperature was 245-275C (475-525F). Now, 240-260C (460-480 F) is more accepted for eutechic (eutechicish) solder. My2� Dave F

Re: Wave soldering temperature

Electronics Forum | Thu Nov 04 14:13:34 EST 1999 | John Thorup

Hi Tim It sort of depends on the solder alloy being used and the particular assemblies being soldered. If you are using the usual 63/37 alloy I would consider 500 to be a bit warm unless the assembly required it. Some alloys would require a higher

Re: High temperature soldering

Electronics Forum | Fri Apr 24 15:21:08 EDT 1998 | Earl Moon

Looking for anyone who has experience with high temperature soldering. Need to determine why solder joints are failing. Thermocycling of unit is -40C to +140C, 30 minute dwell time, 10 sec. transition time Your help is appreciated Ed Holton

Wave soldering preheat temperature

Electronics Forum | Sat Apr 14 00:04:21 EDT 2001 | zam_bri

I'm not a Wave soldering guy and my friend have asked me a question on what is the best preheat time and temperature for Wave soldering.They experiences only 10% flow up thru the PTH barrel. I've asked them to increase the temperatue to 120 Deg C. Cu

Re: High temperature soldering

Electronics Forum | Fri Apr 24 20:33:06 EDT 1998 | D.Lange

Looking for anyone who has experience with high temperature soldering. Need to determine why solder joints are failing. Thermocycling of unit is -40C to +140C, 30 minute dwell time, 10 sec. transition time Your help is appreciated Ed Holton

  1 2 3 4 5 6 7 8 9 10 Next

soldering temperature fr4 searches for Companies, Equipment, Machines, Suppliers & Information

High Throughput Reflow Oven

High Throughput Reflow Oven
Industry 4.0 Reflow Oven

High Precision Fluid Dispensers
Fluid Dispense Pump Integration

Outstanding liquid dispensing and UV curing, all within one platform, watch the video.


Software programs for SMT placement and AOI Inspection machines from CAD or Gerber.
Accurate and consistent volumetric Dispensing System Solutions for 1- and 2-component fluids with ASYMTEK Vortik family of pumps. Learn more.

PCBA services - from simple board assembly to complex product development and testing