Electronics Forum | Thu Sep 27 18:39:30 EDT 2007 | allgood
We're looking at ERP software for our very small proto and small batch shop. Manex is a name that crops up as being specifically designed for CEMS rather than all the rest which are modified from a universal base. The other is DBA Manuafcturing whi
Electronics Forum | Thu Oct 04 20:50:45 EDT 2007 | itaig1
We recently purchased an IBL VPP-M600 vapour phase reflow oven. We currently only have partial documentation and need to know the requirements for the water cooling. ie flow rate, cooling power etc. We also need the spare parts listing and service ma
Electronics Forum | Wed Oct 10 13:42:59 EDT 2007 | schwende
Hi Ian, I am very well connected with the principles at IBL and can probably offer assistance with the documentation you need. The model # is an older generation, but we can supply the information you need. I had a demo of the new lines of IBL Vapou
Electronics Forum | Wed Nov 07 09:19:16 EST 2007 | pjc
Could be not enough peak temp. Do you have a profiler? I'd measure at the BGA joints- drill under board to get access to BGA solder joints and embed a couple of thermocouples with hi-temp solder, then run your profile to see max. temps. and that prof
Electronics Forum | Wed Aug 27 12:57:25 EDT 2008 | adamcrum
I have had this problem with my Vitronics wave and looked into alternatives. Kyzen has a product called Cybersolv 8502 that is made specifically for finger cleaning. I found it to work great. They will send a free sample to you of a pint, but I would
Electronics Forum | Mon Feb 11 17:21:40 EST 2008 | larryd
What causes BGA voids over 25%? Have recommended profile for solder paste, hit 237C for 5 seconds and still get a void on 2% of specific BGA in various locations. BGA is FG676, 1mm pitch, on ImAg using lead free paste OM338 on a 6 layer FR4 PCB.
Electronics Forum | Thu Feb 28 14:27:07 EST 2008 | cyber_wolf
The flux dries out and the paste sticks in the stencil apertures. As the flux dries it also causes the solder to oxidize. Hahaha ! I remember adding flux to paste back in the day to loosen it up. Do not do it ! I have been told by reputable industry
Electronics Forum | Tue Mar 11 16:41:02 EDT 2008 | karkanov
Hi guys Just wanna know what software, technique you use to creat assembly work sheet? do you have develop specific application do you know software where everything is done? do you use Soft like Autocad to draw our board and import the PCB into it?
Electronics Forum | Tue Mar 25 03:14:52 EDT 2008 | vinitverma
Hi Floyd, What is your application? Are you a low mix high volume manufacturer? If yes, then the FCM II is a very good option for high speed. Please write to me offline at vinit.verma@prosemtechnology.com with specific questions that you have in min
Electronics Forum | Tue Apr 01 12:52:34 EDT 2008 | pstone
Thanks for the insight. Most boards we are seeing problems with are 1.60mm thick (some less) and most of them are panelized. For your support pins what do you use to show operators where the pins should be setup? I have heard of using Plexiglas to m