Electronics Forum | Fri Feb 19 03:57:48 EST 1999 | Mark Alder
Please could you suggest a recommended aperture sizes for printing of smd adhesives. Any recommendations on stencil thickness as well as stencil finish will be appreciated.
Electronics Forum | Fri Feb 19 12:56:34 EST 1999 | Tony A
| Please could you suggest a recommended aperture sizes for | printing of smd adhesives. Any recommendations on stencil thickness as well as stencil finish will be appreciated. | Mark, talk to Irene Horvath at I Source Technical Services, Inc. Her
Electronics Forum | Mon Feb 22 12:04:15 EST 1999 | Dave F
| Please could you suggest a recommended aperture sizes for | printing of smd adhesives. Any recommendations on stencil thickness as well as stencil finish will be appreciated. | Mark: About the only rule of printing adhesives is: Keep it off the
Electronics Forum | Tue Nov 29 12:53:56 EST 2005 | bschreiber
Hello Billy, You are correct when you say that you may want to look at the detergent (chemistry) you're adding to the stencil wash. However, "geared for epoxy removal" depends on how the chemistry is designed to remove the epoxy. If it is a "water
Electronics Forum | Fri Apr 30 07:45:15 EDT 2004 | Frederic
Hi all What adhesive you recommend to catch thermocouple to the board? (resistant to high temp and easy remove from PCB) Thank Frederic
Electronics Forum | Fri Apr 30 18:52:22 EDT 2004 | RicardoF
what about 4 cm of kapton tape on each Thermocouple?
Electronics Forum | Fri Apr 30 08:28:39 EDT 2004 | davef
Roger Saunders, President Saunders Technology, Inc wrote a fairly unbiased paper that compared different thermocouple attach methods. You can probably find it on their site. In it, about gluing thermocouples, he says: There are two general classes
Electronics Forum | Fri Oct 01 09:25:50 EDT 1999 | Gian.D
Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... Many tahnks
Electronics Forum | Fri Apr 30 11:55:55 EDT 2004 | Chris Lampron
Hello Fredrick, I have used several methods of TC attachment including quick set adheasives (not good at reflow temps as Dave suggests) long set two part epoxies (work well if you have the time to wait for a sufficiant cure) temprobes, tape (kapton
Electronics Forum | Wed Aug 05 14:55:15 EDT 1998 | john
Probably should have been more specific. We want to do some stencil etching. Mainly for prototype work nothing too high volume. Thanks, Oh yeah, (Ben) and maybe a tattoo here and/or there.. Ha ha ...
winsouce.jpg)