Electronics Forum | Wed Jul 04 11:10:56 EDT 2001 | davef
It�s tough to say. You need enough, but you can�t have too much because you slop it all over the pads, but if you have too little � well you get the picture. There�s so many ways to get to the same place. There is no standard. It�s whatever you n
Electronics Forum | Thu Jul 05 19:39:19 EDT 2001 | davef
I had forgotten that it was you that was on the Sipad adventure. [But then again, who can keep track of yer aliases? ;-)] You just go from one adventure to the next. Expanding On Dave�s Hi-Test Flux Method Theory � PASTE: Yes, contact your favorit
Electronics Forum | Mon Jul 30 21:03:44 EDT 2001 | davef
You should specify the level of res based on the effect of the res on the end-use of the product. J-STD-001 defines cleanliness requirements for ALL flux types, including water soluble and no-clean that you mention. 1 There is no equivalency betwee
Electronics Forum | Wed Feb 02 20:53:34 EST 2000 | Dave F
Dennis: Several points: 1 If you're talking AlphaLevel process (?): � Good solderability, as HASL, even no-cleans bite well. � Planarity, uniform deposit, no bridgin� of FP. � Doesn't store as well as NiAu ... LT 6 months sealed � Very sensitive t
Electronics Forum | Wed Jan 05 11:11:09 EST 2000 | Dave F
Hey Pat: My responses are: 1. Does anyone have experience with the shelf life on immersion white tin? If so, how long can the boards be stored without adversely affecting solderability. I've heard one year. No, we don�t, because we turn boards fa
Electronics Forum | Wed Nov 10 11:31:06 EST 1999 | John Thorup
Hello Horace You're lucky in that you have two of the same machine. You should be able to arrive at the root of the problem by comparison. The problem is likely to occur in one or more of these areas: MACHINE: As said , pump speed and air contact ar
Electronics Forum | Tue Oct 12 16:26:01 EDT 1999 | Jeff Sanchez
| | | | We have three buckets filled with leftover solder paste from our screen printing process. Kester has informed me that they no longer take paste, but only dross and pot dumpings. Does anyone know if there's someplace I can recycle this, or a
Electronics Forum | Tue Oct 05 14:38:06 EDT 1999 | Debbie Alavezos
| | Hi, | | | | Help! Could anyone help to enlighten me on this? | | | | Question: | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a n
Electronics Forum | Sat Oct 02 03:51:28 EDT 1999 | Brian
| | Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? | | It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... | | Many tahnks | | | Don't kno
Electronics Forum | Mon Oct 04 04:37:57 EDT 1999 | Gian.D
| | | Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? | | | It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... | | | Many tahnks | | | | |
The SMTA membership is a network of professionals who build skills, share practical experience and develop solutions in electronic assembly technologies and related business operations.
Training Provider / Events Organizer / Association / Non-Profit
6600 City W Pkwy
Eden Prairie, MN USA
Phone: 952-920-7682