Electronics Forum | Thu Aug 19 23:56:49 EDT 1999 | Earl Moon
| | I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the
Electronics Forum | Fri Aug 20 09:33:51 EDT 1999 | Don Morgenstern
Earl & Jeff Our machine is different than the Electrovert Solder Pak in that it is does not behave like a "volcano". Jeff, please contact me if you have safety concerns as perhaps you also want to consider our equipment. | | I'm trying a second ti
Electronics Forum | Fri Aug 20 13:00:16 EDT 1999 | ScottM
| I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the ad
Electronics Forum | Tue Aug 10 11:44:20 EDT 1999 | John Thorup
| Does anyone use reflow profilers? Are they a good investement or is trial and error sufficient? | | Does anyone have any suggestions on profiles to try? Thanks. | Danielm I would hazard a guess that most if not all of us production folk do. I c
Electronics Forum | Fri Jul 30 16:43:28 EDT 1999 | Dreamsniper
Surface Mount Components like QFP's in Tray usually comes sealed in an anti-static plastic pack. In case the QFP's were removed from the said anti-static bag for more than 2 weeks, do these components needed to be baked for they might produce solder
Electronics Forum | Mon Jul 12 13:06:32 EDT 1999 | Earl Moon
| I had parts replaced on SMT PWBs and the repair created measling defects. | Reliability Question: | Q1. Can measling be aggrevated or grow over time due to | temperature cycling and moisture. Customer environment is | -62C to +85C. | | Thank
Electronics Forum | Fri Jun 25 16:54:25 EDT 1999 | C.K.
| | | Dear John/Earl | | | | | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | | | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the
Electronics Forum | Thu Jun 24 11:29:50 EDT 1999 | Matt Stump
| Hi | Could anyone tell me where i can find information, in the literature or on the Web, concerning measurements of temperature distribution, expansion, stresses in the substrate and heat sink and on the interface between them, that is all the rang
Electronics Forum | Mon Jun 14 15:29:49 EDT 1999 | Sergio Luiz Vito
I am looking for more information about: 1) What kind of evaluation can I do to measure the resistance to fall off of a bottom side glueded SMT component?; 2) There is some influence of doble wave solder machine (temperature, flux, etc) in SMDs fal
Electronics Forum | Wed Jun 16 14:14:07 EDT 1999 | Dave F
| Hello, | I am looking for the surface resistivity and volume resistivity of standard fr4 as a function of temperature and /or humidity . can any one help? | Frank: Sorry I'm so late getting back to you. 1 Use either ASTM D5109-94 or IPC-TM-6