Electronics Forum | Wed May 27 15:09:30 EDT 1998 | Dave F
| | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not locali
Electronics Forum | Tue Dec 01 12:44:15 EST 1998 | Earl Moon
| | | | | All y'll: I could use your input on determining when to skim dross from a wave solder pot. | | | | | | | | | | On one hand, dross protects the surface of the solder from oxidation. On the other hand too much dross may affect solder joint
Electronics Forum | Tue Dec 01 13:53:12 EST 1998 | Brian Conner
| | | | | | All y'll: I could use your input on determining when to skim dross from a wave solder pot. | | | | | | | | | | | | On one hand, dross protects the surface of the solder from oxidation. On the other hand too much dross may affect solder
Electronics Forum | Wed Dec 02 09:03:34 EST 1998 | Dave F
| | | | | | | All y'll: I could use your input on determining when to skim dross from a wave solder pot. | | | | | | | | | | | | | | On one hand, dross protects the surface of the solder from oxidation. On the other hand too much dross may affect
Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Sat Mar 06 08:01:45 EST 1999 | Scott Cook
| Can someone please advise me to the rework procedure for removal and replacing Ceramic Chip Capacitors (e.g. 0805, 1206, etc.)? | | Is it necessary to pre-heat ceramic capacitors before soldering them onto a PCB with a soldering iron? Is this just
Electronics Forum | Mon May 18 21:29:38 EDT 1998 | D.Lange
| I've tried every thing I can think of. Do you have any | Ideas? | What I have is micro balls on the gold fingers of | panelize boards. These balls only appear on the gold | finger. Or at least I can only find them on the gold | fingers. | What I