Electronics Forum | Wed Feb 16 21:51:29 EST 2000 | Dave F
Kurt: Lots of choices, not many of them good, yano. 1 So LPI has taken over the market pretty nearly 100%, but it won't "tent" reliably, because it is not very viscous when applied and drops into the hole. So then, tenting/plugging with LPI is bad
Electronics Forum | Mon Feb 26 20:02:42 EST 2001 | davef
First, I don�t understand why your board fabricator can�t do a good job plugging your vias. Additionally, when you consider that they forgot to plug the first batch of boards, it makes me wonder if they are desirable as a supplier. Generally, we us
Electronics Forum | Sat Oct 09 09:07:48 EDT 1999 | Brian
| | | Can anyone tell me the formula/method to determine | | | the amount of weight that solder's surface tension can support. | | | (ie: Maximum weight of components soldered onto a bottom side | | | of a board during a top side reflow on a Paste/Pa
Electronics Forum | Sat Oct 09 09:18:21 EDT 1999 | Dave F
| | | | Can anyone tell me the formula/method to determine | | | | the amount of weight that solder's surface tension can support. | | | | (ie: Maximum weight of components soldered onto a bottom side | | | | of a board during a top side reflow on a
Electronics Forum | Sun Oct 10 18:53:04 EDT 1999 | Dreamsniper
| | | | Is there an IPC Standard stating the max. number of times that a PCB can pass through a reflow or wavesolder machine without having solder mask breakdown. | | | | | | | | PCB is FR4 | | | | Solder Mask is LPI | | | | Reflow and W/S Profile =
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Thu Aug 19 22:59:48 EDT 1999 | Jeff Ferry
| I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the ad
Electronics Forum | Thu Aug 19 23:56:49 EDT 1999 | Earl Moon
| | I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the
Electronics Forum | Fri Aug 20 09:33:51 EDT 1999 | Don Morgenstern
Earl & Jeff Our machine is different than the Electrovert Solder Pak in that it is does not behave like a "volcano". Jeff, please contact me if you have safety concerns as perhaps you also want to consider our equipment. | | I'm trying a second ti
Electronics Forum | Fri Aug 20 13:00:16 EDT 1999 | ScottM
| I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the ad