Electronics Forum | Fri Aug 27 09:40:58 EDT 2004 | cyber_wolf
Hey Harry, This is interesting....I left your secretary 2-3 messages over the last moth or so to purchase one of those 5 processor boxes from you. Do you no longer require our business, or are you just not getting your messages? Not that I really c
Electronics Forum | Fri Aug 27 12:42:12 EDT 2004 | valuems
Hello Sr. tech We haven't received any e-mails or calls from you that we know of. Yes once in a while one does fall thru the cracks. If that did happen we are sorry. I make a lot of service calls on MPM's and live on the cell phone. Thanks for yo
Electronics Forum | Tue Aug 24 09:04:59 EDT 2004 | Dreamsniper
I agree with Rob's Common Parts Report and purchasing should be aware that with common parts a single reel parts will not work. They need to stock more supply or if this part is a common part and of low quantity (say 2 per PCB for 6 different product
Electronics Forum | Wed Aug 25 09:45:03 EDT 2004 | rlackey
Wow, you really can do great things with Meccano. Thats it, I'm throwing away all 8 of my ultra fast bomb proof Fujis and swapping them for a brand new Fisher-Price "My First SMT Machine". Cheers Greg, I've now seen the light!
Electronics Forum | Wed Aug 25 12:04:35 EDT 2004 | stefwitt
I like that feature, good thinking, but can your machine print barcode labels as well? If you tear down a job and set up a new one, you could attach these labels to each reel and tag the remaining quantity of components, before they go back to the st
Electronics Forum | Mon Aug 30 20:05:25 EDT 2004 | justathought
All of these options are great for the C5 but.... are there any service issues we should know about? Like can you service them? Greg you said the C5 is rated at 22,000 CPH is this true of the single head design or just the unfinished dual head design
Electronics Forum | Tue Aug 24 13:45:17 EDT 2004 | Indy
Hi, I am trying to assemble a LTCC component with Pd/Ag surface finish on to Sn/Pb/Ag solder and Sn/Ag/Cu solder. I am passing it through a reflow. I have observed poor wettability at the solder-pad joint. Does anyone have information regarding th
Electronics Forum | Tue Aug 24 13:47:14 EDT 2004 | Indy
Hi, I am trying to assemble a LTCC component with Pd/Ag surface finish on to Sn/Pb/Ag solder and Sn/Ag/Cu solder. I am passing it through a reflow. I have observed poor wettability at the solder-pad joint. Does anyone have information regarding th
Electronics Forum | Tue Aug 24 13:47:16 EDT 2004 | Indy
Hi, I am trying to assemble a LTCC component with Pd/Ag surface finish on to Sn/Pb/Ag solder and Sn/Ag/Cu solder. I am passing it through a reflow. I have observed poor wettability at the solder-pad joint. Does anyone have information regarding th
Electronics Forum | Tue Aug 24 16:06:09 EDT 2004 | Robert Ack
Being a surface mount department manager for well over 6 years I have seen this countless times. While we run mostly water soluble I havent seen any negative issues while running boards through the oven twice. Sometimes we even spray an additional am