Electronics Forum | Mon Mar 19 08:56:17 EST 2001 | fmonette
One very important consideration in your situation is to determine if you have moisture sensitive components on these boards. If you have any device classified level 3 or higher then you have a very high level of risk associated with moisture sensit
Electronics Forum | Mon Mar 19 21:06:17 EST 2001 | davef
Liken soldering fumes to cigarette smoke. These fumes consist of two elements. 1 Smoke particles [very sticky] 2 Gases and vapors Particulate Filters: Smoke particles can be removed with a particulate filter. All particulate filters are graded u
Electronics Forum | Wed Mar 21 16:32:03 EST 2001 | mparker
The root cause is dependant on the type of solder "splash", ball, whatever, that you are seeing post reflow. If it is smears, then cleaning the stencil underside is probably the answer. Are you using automatic wipers? How many print cycles between w
Electronics Forum | Fri Mar 23 11:58:01 EST 2001 | mparker
You are mixing long exposed paste back into fresh? How long has your fresh jar been open to the air? You are probably doing yourself a disservice by scavenging the paste (it could have moisture entrapped). Your visocity has definitely changed. You a
Electronics Forum | Sat Mar 24 00:50:24 EST 2001 | PeteC
Fresh paste from a factory sealed container. Should paste be scrapped out altogether if left on the stencil for too long (length-of-time?)? Our paste is Multicore CR39. Multicore reccomended the print chamber be around 22C @ 50%-60% RH. Our plant is
Electronics Forum | Tue Mar 20 09:31:56 EST 2001 | PeteC
I dunno.: e�lec�tro�lyt�ic Of or relating to electrolysis. Produced by electrolysis. Of or relating to electrolytes. e�lec�trol�y�sis Chemical change, especially decomposition, produced in an electrolyte by an electric current. Destruction
Electronics Forum | Thu Mar 22 14:12:09 EST 2001 | slthomas
Interesting...the very reason we use water soluble paste on some of our boards is for that reason, although I've never been able to get anyone to show me something in print that supports it. It's just what engineering has told me. We currently have
Electronics Forum | Thu Mar 22 16:35:06 EST 2001 | Steve
Deja vu! When I read your response I turned around to see if you standing behind me listening to our problem. We currently make about 50 different boards all using no-clean that have no problems, yet this newest boards has a couple of issues that eng
Electronics Forum | Thu Mar 22 17:37:06 EST 2001 | davef
Hey!!! Watch it!!! I don�t want to get you believing too much of this stuff. But if you bought that, listen to this � some circuits are so critical with that skin effect stuff that they use silver as the top level solderability preservative. Turn
Electronics Forum | Wed Mar 21 20:40:28 EST 2001 | dblsixes
We are building a monster ... Dimensions are 10" x 7" ... 12 layers ... A Logic Assembly with a Power Supply all rolled into one ... The Power Supply is in one section of the board, the logic in the other section ... The Power Supply obviously has a