Electronics Forum | Tue Mar 07 10:46:24 EST 2006 | muse95
I have to disagree with you, BillyD. If Craig searches the forum, he will see that the concept of a Pbfree BGA with SnPb paste has been debated many times. You say it is fine. I say it is NOT. There have been several studies done that clearly sho
Electronics Forum | Mon Mar 13 10:45:44 EST 2006 | muse95
The original issue was Co. does not need to go Pbfree, but some BGA's they use are only available Pbfree. They don't want to throw away Pb BGA stock, so some boards might have a combination of both Pb and Pbfree BGAs. The question basically was Shou
Electronics Forum | Tue Mar 07 15:11:43 EST 2006 | davef
We wouldn't know a Gemini from a bread box, nor we are real clear on what you seek. So, we'll just rattle on for a while. Here's how we monitor the quality of our dispensing process: * We dispense the same nonfunctional pattern of dots on every boa
Electronics Forum | Sat Mar 11 11:10:05 EST 2006 | eolparts
Hello All, I sent Grant an e-mail and I wanted to share with you. My name is Jim Schreiber and I am the product mgr at EOL Parts Inc. We have access to over 1000+ OEM and CEM excess/surplus inventories that we use on a regular basis to pass on cost
Electronics Forum | Wed Mar 08 14:11:38 EST 2006 | mholz
I am looking for an industry standard �stock� note to place on our printed circuit board assembly drawings that will capture a level of cleanliness for an IPC-A-610 class 2 board assembly. I�m looking for some quantitative spec for cleanliness that w
Electronics Forum | Thu Mar 09 00:45:57 EST 2006 | kent_peterson
Fastek will get it done with 2 machine and 2 shifts. 2 shifts would need to place 50,000cph. One CP643 with both device tables set could get it done. Having it panelized in 50's, you would need to print 50 panels a hour so get a auto cleaner on the p
Electronics Forum | Thu Mar 09 12:09:19 EST 2006 | fastek
I assumed a conservative 25,000 cph for each of the chipshooters...whether it's an MV2F, CP-6, CP-642 etc. You're not going to get 50,000 cph out of (1) CP-643. You might for short periods but not in the long run. It would be suicide to rely on one
Electronics Forum | Tue Mar 14 03:57:43 EST 2006 | Base
Hey Peter, Did some simple math... 800.000PCB's x 20cmp = 1.6million placements 8hrs/day * 22 days/month = 176 hrs You're looking at over 90kCph fulltime! I'd say go with an AX-5 as JAX suggested. Given the product you described you could reach s
Electronics Forum | Mon Mar 13 04:49:59 EST 2006 | Fhail
Hi All, I'm new in PCBA process. Recently in my leadfree production we encountered a missing ring on some of the ring on the board after we ran hem through Wave soldering machine. The board has gone through double reflow prior to the Wave soldering.
Electronics Forum | Tue Mar 14 13:42:45 EST 2006 | patrickbruneel
If the OSP boards have gone through double reflow I assume that you use an aggressive (halide) flux for wave soldering. SAC 305 is known (search the archives) to dissolve copper faster than other lead-free alloys. This together with an aggressive flu