Electronics Forum | Tue Sep 16 19:13:28 EDT 2008 | hegemon
Our Mirtec MV3 Benchtop machine came with its own table. Others may or may not. During our evaluation of AOI machines we had 2 other units set up on standard workbenches at times. A solid, shake free table is a MUST, the heavier the better. There i
Electronics Forum | Tue Sep 23 15:27:17 EDT 2008 | slthomas
You'd still have to change all of the part library references, make up new ones for new parts, enter feeder sizes, etc. More trouble than it's worth, once you know how to use the software and prep your cad data to be compatible with it. There are lo
Electronics Forum | Fri Sep 19 15:52:18 EDT 2008 | davef
This is not something that we'd expect to see on NiPdAu finished leads. Help us understand the extent of the problem better. From your picture, it looks like a band of copper color with black on the outer portions of the copper color that bleeds int
Electronics Forum | Fri Sep 26 16:34:16 EDT 2008 | aqueous
Its not likely your air quality that lowers the test solution's resistivity. Maintaining 60 M-Ohm requires almost constant circulation through DI resin beds. Just natural CO2 (Carbon dioxide) absorbed by the test solution will lower the resistivity
Electronics Forum | Thu Oct 02 08:24:32 EDT 2008 | rway
If you want to go really cheap, you could try Pace Systems. You can get a three channel system, hot air, desolder and soldering iron. Or any other combination handpieces that they offer, for around $3K. They also have power supplies with a single
Electronics Forum | Fri Oct 03 16:51:06 EDT 2008 | waveroom
If this is a one time rework might I suggest farming it out? 100pin QFP can be taken off no problemo.. Putting it back down properly and then hand soldering??? I wouldn't want that job. You need excellent placement and imaging and your not going to
Electronics Forum | Thu Oct 02 01:47:57 EDT 2008 | myleb
I'm new to SMT. Now, i'm making program for SPI machine to inscpect for solder paste of SP60-MU. I think this is a very good printer but some times, my program shows only 50-60% of volume transfer; and the average height is very high: nearly 200 pct.
Electronics Forum | Thu Oct 02 08:09:04 EDT 2008 | pwilson1
Hi All, I am currently in the process of selecting a new stencil printer and have narrowed it down to the MPM125 or DEK Horizon 03i.. We re a UK medium volume production facility running quite a high mix of double sided PCB`s. W
Electronics Forum | Wed Oct 08 12:41:08 EDT 2008 | sambolian
I having trouble with the Quad IIc. After manually teaching a program at the machine, I upload to save it, then when I go to "Run System", it downloads the program, but then an error comes up saying "Fiducials not taught, press ESC to abort". I've tr
Electronics Forum | Thu Oct 23 12:50:28 EDT 2008 | gregoryyork
Hi Dave sorry not been back the Tin/P regenerator is controlled amounts of Phos additive that metallurgically reduces the dross. We do not recommend chemical methods for dross reduction as many salts/chemicals used could be hygroscopic in nature and