Electronics Forum | Mon Oct 18 11:43:42 EDT 2010 | hegemon
Use the forums nice search feature above. "Lead Free BGA" Lots of info. In short it seems the general consensus is that you are pretty much safe using your lead free BGA in a tin lead process, provided you run your peaks a little higher, and your
Electronics Forum | Wed Dec 07 17:43:31 EST 2011 | mikenil
Hi I do not work for a board house but a manufacturing facility where we do a considerable amount of soldering wires to through holes. We pretin our through holes on both sides of the PCB prior to reflowing the solder and installing the conductor (w
Electronics Forum | Tue Dec 13 15:18:32 EST 2011 | ck_the_flip
DaveF, That's correct. This assembly is plain old tin-lead, but our buyer purchases the bare PCB with lead-free HASL plating. My main concern was the regular tin-lead not coalescing with the PCB plating and having a weak intermetallic. I'm not fr
Electronics Forum | Tue Nov 06 22:37:35 EST 2012 | davef
Ryan ... "As for bismuth-based lead-free alloys, a lower melting temperature than that of tin-lead is offered together with a cost similar to that of tin [in the area of $3/lb]. Unfortunately, bismuth in soldering alloys tends to create embrittlemen
Electronics Forum | Mon Nov 10 09:03:47 EST 2014 | rgduval
I can't claim to be an expert....I've just bought a used RPS, and it'll be my first...but, after reading through their manual, and working on setting things up, I'd say: -Conceptually, I like the idea of moving the board rather than moving the entir
Electronics Forum | Tue Feb 14 01:00:47 EST 2017 | soldertraining
Soldering Bath - When we need to tin high-power contacts or a lot of wires, for example, in making harnesses, a regular soldering iron is either impossible to use due to the high thermal capacitance requirement, or takes way too long to perform the t
Electronics Forum | Mon Nov 27 22:01:25 EST 2017 | bibi11952
Hello SMTNet, We had received boards from our CM, some came with a Tin plated finish on the SMT hermaphroditic edge connector, while others came with Gold plated on the same connector. Tyco supplies both version and they apparently mixed up parts.
Electronics Forum | Tue May 21 13:17:47 EDT 2019 | SMTA-Thomas
2.54 μm [100 μin] gold thickness and all through-hole leads that will be hand soldered regardless of gold thickness” (we automatically solder wash all components which violate this requirement). In all cases we have attempted different no clean flux
Electronics Forum | Wed Dec 11 06:47:33 EST 2019 | ameenullakhan
Dear Friends, Need your valuable feedback on how to identify the component is ok or not for manufacturing. Issue : We have parts which are more than 5 years old.And management want us to qualify this parts for production. We presently use below me
Electronics Forum | Wed Feb 12 14:38:18 EST 2020 | SMTA-Alex
There are several areas you can check. Your profile is very fast. You reach the peak at around 3 minute mark. That's not enough time for the fillet to form. Try to slow down your belt speed to around 90-95, to give it more time. Also, your temperatur