Electronics Forum | Thu Mar 17 10:56:24 EST 2005 | jmedernach
Hi John, This problem is interesting. I've never had a problem with solder shorts caused by subjecting a device to reflow a second time. I've built many double sided SMT assemblies with fine pitch devices on top and bottom. Some things to possibly
Electronics Forum | Fri Mar 18 14:21:02 EST 2005 | Dreamsniper
We are producing control products for the Aerospace Industry both Commercial and Military. I have TQFP 100 fine Pitch in one of my PWB's Solder Side and have no misalignment problems or defects on my part after 2nd reflow. I control my reflow profile
Electronics Forum | Mon Apr 18 14:58:36 EDT 2005 | halal
I have checked the links that you and Will gave to me. I have new info about my task: The task is to summarize the mask aligning methods. The first method: The factory already has an UV machine for the exposure, so they search some positions with a
Electronics Forum | Thu Apr 14 06:54:02 EDT 2005 | teera
hi! below are the item need to check: 1)top plate condition(under screen squeegee). 2)under screen clean contact position(with stencil) 3)make sure the thickness of wiper paper not so thick(not over 6o gm)becaue it will effect the vacuum suction. 4)s
Electronics Forum | Thu Apr 21 04:16:17 EDT 2005 | Infinity
Dear all, I am doing some small business selling solder paste, chip capacitors and resistors in China. I am going to expand the existing SMT product line. Can you experts throw in some ideas? For example, what other products would you all think of
Electronics Forum | Tue May 03 10:57:22 EDT 2005 | Frank R.
We received about 5K assembly boards from china. They left flux residu on top of the board and the flux they use was different than us. RESULT ... we use a translucent cylicon to cover the board and it was not possible to dry the cylicon because of
Electronics Forum | Wed May 04 09:37:08 EDT 2005 | MikeaJ
I would not recommend trying to cram or mix and match multiple images on a stencil. Especially if you are a contract house, and your clients don't understand why sending one board seperate from a panel of four is a pain in the face. However, I have h
Electronics Forum | Tue May 03 15:19:12 EDT 2005 | cuculi54986@yahoo.com
Thanks for the suggestions. We have been going around the dome to pick from the base. The placement machines are Panasonic chipshooters - MV2VB and MV2C. I have several problems with the MV2C. The K-type feeder plates were moved by my predeces
Electronics Forum | Mon May 09 17:27:46 EDT 2005 | cmiller
They are expensive so you need to have a lot of jobs that take a long time to hand solder or have a ton of masking. Also look at bottom side wave soldering, if you are having a lot of defects, the selective will allow you to solder both sides in surf
Electronics Forum | Tue May 17 10:11:54 EDT 2005 | russ
I would use a foam fluxer since spraying rosin will make the stickiest nastiest mess you can imagine. 18 layer board huh? You will want convection preheat, both top and bottom preheaters, preheat tunnel of at least 4-5', a chip wave, laminar flow w