Electronics Forum | Thu Aug 30 13:26:40 EDT 2012 | joeherz
Appreciate all the replies. We have a good system in place with ESD tile floor, grounded systems/benches/etc and heel and wrist strap usage and monitoring. Good training program as well. We've recently upgraded to the 2007 version of the ANSI 20.2
Electronics Forum | Thu Sep 13 21:18:16 EDT 2012 | vergara1
Hello, I was looking at your photos of this diode. I have a two question and I'm sure it maybe a simple fix. One, Is the diode actualy touching the pad;reason I ask is, I see that theres excessive amount of adhesive underneth the part. Two, did you
Electronics Forum | Wed Sep 26 10:05:41 EDT 2012 | testbloke
Although we do not have any soldering issues with our OSP PCB's, I am trying to establish clear rules with regards pcb storage and shelf life. Our PCB's are supplied in metalised moisture barrier bags but without desicant, our current rules as follow
Electronics Forum | Mon Oct 29 15:41:08 EDT 2012 | mbnetto
Hello, Here in our factory we have a line with 3 mydatas MY9 in series. I'm trying to do a optimization of a new product but I'm facing some problems. I noticed that after the optimization the software is considering all the components that use onl
Electronics Forum | Wed Nov 07 15:01:18 EST 2012 | nikyta
Thanks Dave , my question is about Spopov want to try "Lead Free" SnBi (but uses it on Leaded finishes), but is worry about its low melting point (at this point, no longer 138 degrees as he wrote, but rather in an unknown and unpredictable range bet
Electronics Forum | Fri Nov 02 16:22:49 EDT 2012 | jorge_quijano
Hi folks, I'm trying to develop a method to evaluate new SMT equipment, we will need to invest in a new SMT line soon, so I have to evaluate what machines would fit our manufacturing process, I'm thinking in create a matrix and evaluate every machine
Electronics Forum | Tue Nov 13 12:02:54 EST 2012 | jaimebc
I'll try swaping cards and see if the problem follows the card. So far, my guess would be the motor going bad. I did change the brushes, X wagon cables and every cable that goes to the midas unit. But that didn't fix it. The problem is that to replac
Electronics Forum | Thu Nov 15 10:19:05 EST 2012 | davidmercader
Hi, We have problems with our wave soldering process. The problem is that during the same assembly, after wave soldering, some pcb’s look not clean and other pcb’s look good. We use lead free SAC305 solder and flammable flux. We think our proces
Electronics Forum | Mon Dec 10 13:26:40 EST 2012 | dyoungquist
We are using our selective solder machine to solder a backplane with sixteen (16) 4x48 pin 0.080" connectors. Our first pass yield is about 85% meaning that 85% of the connectors come out with no bridges. Not quite as fine pitch as your connector a
Electronics Forum | Fri Feb 01 19:07:57 EST 2013 | hegemon
We have had some success in void reduction with LGA by pre-tinning or "bumping" the devices before placement. The extra solder seems to allow a slightly higher standoff, and allows better outgassing, is my guess. A lot more labor , but the results