Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
Electronics Forum | Thu Dec 21 13:06:16 EST 2006 | vortex
Hi we are a small contract manufacturer in need of a one time use cable crimping tool DF13-TB2630HC. We only have 3 (4) contact wires to make which will be plugged into another assembly. The p/n we are trying to crimp is DF13-2630SCFA. If you have th
Electronics Forum | Fri Jan 05 13:15:59 EST 2007 | jhaviland
Depends on your company's IT policies. I have seen some companies where IT will not touch a production PC since it was not a standard IT issue PC, I have also seen some companies IT department do normal backups of the machines. (personally) whoever c
Electronics Forum | Tue Jan 09 13:01:17 EST 2007 | stepheniii
Not unless it's a case of "the only difference is..." What I mean by that is more than once I've been told the only difference in a new rev is one component or one change. But the truth was that was the only reason for the change, and in fact there
Electronics Forum | Thu Jan 11 18:16:40 EST 2007 | slthomas
I won't even guess, but I would suggest that if you don't get much help here (pretty tough question), you might try dogging somebody at IPC. They seem to have a pretty good handle on that kind of stuff. All I know for sure is that we shipped a worki
Electronics Forum | Mon Jan 15 11:12:08 EST 2007 | jaimebc
I've had experienced this issues here with our GSM's Flex heads. Try this: 1.- Clean your linear scales with alcohol and a lint free cloth. Both the X and Y. This one has fixed the majority of our errors when one of the heads just stops for no apare
Electronics Forum | Tue Jan 16 18:18:46 EST 2007 | greg york
Sorry that answer never really gave you the reason and ways to resolve. Reason - most composite pallets are only good up to 180C so thermal excursions at 250 or even 270c lead free kill them. Try to stay on top of cleaning as well and some pallet mat
Electronics Forum | Wed Jan 17 15:13:24 EST 2007 | jaime39
When placing the part to be reflow try applying heat to the board from the secondary side until the primary side has a temperature of about 130 degrees celcius. Following this procedure it should minimize the heat exposure of the part being soldered.
Electronics Forum | Thu Jan 18 05:35:22 EST 2007 | joseluis_amper
Dear friends, I'm from Spain and, in this moment, we try to decide what AOI we need. We had in floor, in Demo, the SAKI, and it was good. But we want to test more machines, and I heard about Omron, Modus, Mirtec.....We have a litle production but so
Electronics Forum | Tue Mar 06 12:58:05 EST 2007 | gregp
Hmmmm, Chicago in February or southern Cal? If I'm getting on a plane anyway I'll go the extra few hours. The show was actually very good for us. We don't look at overall show attendance we look at number of quality leads (which there were many).