BGA Installation with IR unsolder

Electronics Forum | Sat May 17 11:11:42 EDT 2008 | azimi789

would anybody guide me about soldering and unsoldering the BGA ic with Infrared unsolder dais please? in what range of temp. and time I should set the device? (ZORAN Quatrro 4110)

BGA Installation with IR unsolder

Electronics Forum | Wed May 21 20:52:17 EDT 2008 | davef

Did you get the solder to the temperature? Determine the temperature of the solder with a thermocouple.

BGA Installation with IR unsolder

Electronics Forum | Thu May 22 02:25:15 EDT 2008 | lococost

No, absolutely not. The BGA balls should collaps by theirselves. No external pressure should ever be applied.

BGA Installation with IR unsolder

Electronics Forum | Mon May 19 08:18:22 EDT 2008 | davef

You should set the temperature at liquidus point of the solder used on the BGA plus 20 to 25*C. So, for tin-lead that would be ~215*C. Most lead-free solders run about ~20 to 25*C higher than that.

BGA Installation with IR unsolder

Electronics Forum | Tue May 20 10:27:29 EDT 2008 | azimi789

I just set that as you said, but the component doesn't stick on the board. I use AMTECh Flux type: RMA-223.. what should I do ? Thanks.

BGA Installation with IR unsolder

Electronics Forum | Thu May 22 01:37:31 EDT 2008 | azimi789

I found out that the light is not heterogeneous, i am trying to solve this problem... from my web surfing I encountered an article that claimed there should be 200 grams Placement Pressure on the BGA while soldering ... is that really needed? 200 gr

Wave Profile

Electronics Forum | Mon Oct 13 15:34:22 EDT 2003 | John

Anyone ever noticed a difference in measuring the temperature on a soldered board vs. using an unsoldered mole in their wave? I've been looking at the temperature of a specific part, and it reads much higher on an unsoldered mole vs. a soldered mole

Chip Components with big ground pads - Unsolder

Electronics Forum | Wed Jan 28 20:26:32 EST 2004 | Vinny

Hi Guys, Really need your help to suggest how to tackle this situation.

unsoldered joints

Electronics Forum | Tue Sep 22 06:07:02 EDT 1998 | jacqueline coia

need advice to point me in the correct direction for solution to the problem of unsoldered joints which look soldered under normal visual inspection, but when pull strength test is performed the leads are coming away from pad, no strong intermetallic

imm. silver

Electronics Forum | Thu Aug 29 20:02:58 EDT 2002 | davef

Often assemblers leave areas unsoldered for future component additions, modifications, and test points. On imm silver boards, these unsoldered areas become a real bear to solder/test later in life. One way to avoid that problem is deposit some solder

  1 2 3 4 5 6 7 8 9 10 Next

unsolder searches for Companies, Equipment, Machines, Suppliers & Information

SMT feeders

Have you found a solution to REDUCE DISPENSE REWORK? Your answer is here.
SMT spare parts - Qinyi Electronics

Benchtop Fluid Dispenser
Equipment Auction - Eagle Comtronics: Low-Use Electronic Assembly & Machining Facility 2019 Europlacer iineo + Placement Machine  Test & Inspection: Agilent | Tektronix | Mantis Machine Shop: Haas VF3 | Haas SL-20 | Mult. Lathes

Software for SMT placement & AOI - Free Download.
2024 Eptac IPC Certification Training Schedule

Best Reflow Oven
SMT spare parts

500+ original new CF081CR CN081CR FEEDER in stock