Electronics Forum | Sun Mar 12 01:58:44 EST 2006 | grantp
Hi, We have been soldering lead free BGA's onto products with lead based paste, and we have had no increase in defects at all. We have used a standard lead paste profile, so we are not altering the temps anything from what's recommended by the paste
Electronics Forum | Tue May 01 09:58:20 EDT 2007 | rgduval
Basem, I can't direct you to a dispensing machine, as I'm not familiar with them. But, I can tell you what we do. We specialize in short volume, prototype quantity runs. Since prototypes and short quantities are not conducive to volume operations
Electronics Forum | Fri May 04 02:32:10 EDT 2007 | jmelson
Thanks! Well, the procedure in the book says to first calibrate the mech aligner with the beam sensor, but that exceeds the X travel. I guess you can just eyeball it off the nozzles and then use trial and error. While poking around on the machine
Electronics Forum | Sat Aug 25 08:39:15 EDT 2007 | gsala
If plastic Carrier Tape (CT)/ emboss tape, is made by: a)Polycarbonate material, it can withstand temperature around 120C� or may be more mantaining original dimension. b)Polystirene material, at max 45�C-50C� the CT starts to change dimensions and
Electronics Forum | Sat Sep 22 01:30:31 EDT 2007 | mika
I am sorry my friend, but I can't recall that specific error number. But it would help if you explain a little bit more about your problem. Remember that an error code Do Not necessary points to a direct root-cause of a problem. First of all we nee
Electronics Forum | Wed Oct 10 17:47:49 EDT 2007 | jmelson
Does it give any more info about the error? Is this in the stage after you've hit run, it says "initializing" and it is counting up on the screen? Usually it gives a little more info, although it can still be cryptic. I have run into it stopping w
Electronics Forum | Thu Jan 03 17:00:20 EST 2008 | davef
Recommended procedure for soldering stainless steel [Atlas Steels Australia]: * Surfaces must be clean and free of oxidation. * A rough surface improves adherence of the solder, so roughening with grinding wheel, file or coarse abrasive paper is reco
Electronics Forum | Thu Sep 11 11:34:52 EDT 2008 | patrickbruneel
Interesting observation Manuel. I will be blamed again for crying wolf but look below a lot more defects will soon see the daylight all related to lead-free. This information was posted at the tin whisker forum by Bob Landman of H&L Instruments.
Electronics Forum | Wed Sep 17 13:00:25 EDT 2008 | mw_fl
For the most part there would not be a lot of change over. There are two primary boards at this time that would be run on the line that also use common components. At this point all but a couple of the pick and place machines we have looked at have t
Electronics Forum | Thu Jan 29 19:01:51 EST 2009 | stevek
Allow me a contrary viewpoint. I've had these things on my floor and had customers get outsourced evaluations done with them. Most expensive boat anchors I've run across. First the good points: The automated scanning and pattern recognition is go