Electronics Forum | Mon May 03 17:09:50 EDT 1999 | Wayne Bracy
| | How's the "Great Gas-out" going for ya'll? | | | | Myself, I'm doing real good! Haven't farted all day...(GRIN) | | | | Anyways, a thread got started down below about this so-called "Lead Free" stuff, and I just wanna' put my two cents in about
Electronics Forum | Sun Apr 25 11:30:12 EDT 1999 | Earl Moon
| Hello all, | | Our guys here still have some questions on the "optimized" profile which sees a more moderate ramp up straight to reflow temperatures versus the conventional profile which has a plateau at around 150 Celsius. If the optimized profi
Electronics Forum | Fri Apr 23 15:33:50 EDT 1999 | C.K.
| | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free soldering on t
Electronics Forum | Mon Mar 01 22:24:53 EST 1999 | Dave F
| It seems to be that we have to much NaCl left on our assambled PCB's. | The flux we use is from cobar. They say it can not be from the flux... So what can be the reason, what kind of problem may occer when there is to much NaCl. | George: When so
Electronics Forum | Mon Feb 22 14:21:14 EST 1999 | Rick Wyman
| | Hey all- | | | | My question is this: My stencil printer operator has said that he has to | | wipe our 6-mil stencil each pass to get the paste in the 20-mill pitch | | aperatures for a QFP to release well. We are using Amtech NC-559 type 3 |
Electronics Forum | Fri Jan 15 10:52:27 EST 1999 | John
| Hi all, | | I thought I'd use this forum to ask a couple general questions on fluxes for manual operations: | First - Is it OK to use a wave soldering type flux (specifically OA)? Thinking about activation temperatures and the ramp rate of the wav
Electronics Forum | Fri Aug 07 07:52:15 EDT 1998 | Earl Moon
| | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not e
Electronics Forum | Wed Dec 05 17:23:41 EST 2001 | davef
Now there�s a conundrum. You want the �best way to clean leads�, but you want to use the worst type of flux for cleaning leads. You say, �20% copper exposed� � * What happened to the solderability protection during this two-year storage? Wouldn�t
Electronics Forum | Wed Feb 26 23:59:48 EST 2003 | Mike Konrad
Grant, No-Clean paste + IPA = White Residue! #1: Stop using IPA #2: Switch to either a solvent-based de-fluxing chemical or an aqueous-based de-fluxing chemical. If you are using an ultrasonic cleaner for your boards as stated, do not use sapon
Electronics Forum | Thu Apr 10 05:25:43 EDT 2003 | dst
Hi, My company is currently experiencing a high feild failure rate on a 100nF chip ceramic that we use in various applications across our product range. One of them being de-coupling which means we use millions of this device every month. The failu
.gif)